Constellium ALPLAN® 7075 High-Strength Rolled Precision Aluminum Plate, Milled Both Sides

Category Metal , Nonferrous Metal , Aluminum Alloy , 7000 Series Aluminum Alloy
Manufacturer Constellium
Trade Name ALPLAN®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Constellium ALPLAN® 7075 High-Strength Rolled Precision Aluminum Plate, Milled Both Sides.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ALPLAN® 7075 precision plates combine a good dimensional stability with high mechanical strength. Both the outstanding flatness and the low roughness of the surfaces, protected by a plastic film, make surface milling by the end user superfluous. This combination of properties enables significant cost savings in machining. Applications include reference plates, machine housings, transport tables, jigs, robot arms.Information provided by manufacturer
Physical Properties Metric English Comments
Density 2.81 g/cc
0.102 lb/in³
Mechanical Properties Metric English Comments
Hardness, Brinell 175

@Thickness 9.90 - 25.0 mm
 175

@Thickness 0.390 - 0.984 in
175

@Thickness 25.0 - 60.0 mm
 175

@Thickness 0.984 - 2.36 in
175

@Thickness 60.0 - 80.0 mm
 175

@Thickness 2.36 - 3.15 in
Tensile Strength >= 495 MPa

@Thickness 60.0 - 80.0 mm
 >= 71800 psi

@Thickness 2.36 - 3.15 in
 Temper T651; Standard EN 485-2
>= 525 MPa

@Thickness 50.0 - 60.0 mm
 >= 76100 psi

@Thickness 1.97 - 2.36 in
 Temper T651; Standard EN 485-2
>= 530 MPa

@Thickness 25.0 - 50.0 mm
 >= 76900 psi

@Thickness 0.984 - 1.97 in
 Temper T651; Standard EN 485-2
>= 540 MPa

@Thickness 9.90 - 12.5 mm
 >= 78300 psi

@Thickness 0.390 - 0.492 in
 Temper T651; Standard EN 485-2
>= 540 MPa

@Thickness 12.5 - 25.0 mm
 >= 78300 psi

@Thickness 0.492 - 0.984 in
 Temper T651; Standard EN 485-2
540 MPa

@Thickness 60.0 - 80.0 mm
 78300 psi

@Thickness 2.36 - 3.15 in
 Typical Strength
565 MPa

@Thickness 25.0 - 60.0 mm
 81900 psi

@Thickness 0.984 - 2.36 in
 Typical Strength
575 MPa

@Thickness 9.90 - 25.0 mm
 83400 psi

@Thickness 0.390 - 0.984 in
 Typical Strength
Tensile Strength, Yield >= 420 MPa

@Strain 0.200 %,
Thickness 60.0 - 80.0 mm
 >= 60900 psi

@Strain 0.200 %,
Thickness 2.36 - 3.15 in
 Temper T651; Standard EN 485-2
>= 440 MPa

@Strain 0.200 %,
Thickness 50.0 - 60.0 mm
 >= 63800 psi

@Strain 0.200 %,
Thickness 1.97 - 2.36 in
 Temper T651; Standard EN 485-2
>= 460 MPa

@Strain 0.200 %,
Thickness 9.90 - 12.5 mm
 >= 66700 psi

@Strain 0.200 %,
Thickness 0.390 - 0.492 in
 Temper T651; Standard EN 485-2
>= 460 MPa

@Strain 0.200 %,
Thickness 25.0 - 50.0 mm
 >= 66700 psi

@Strain 0.200 %,
Thickness 0.984 - 1.97 in
 Temper T651; Standard EN 485-2
465 MPa

@Strain 0.200 %,
Thickness 60.0 - 80.0 mm
 67400 psi

@Strain 0.200 %,
Thickness 2.36 - 3.15 in
 Typical Strength
>= 470 MPa

@Strain 0.200 %,
Thickness 12.5 - 25.0 mm
 >= 68200 psi

@Strain 0.200 %,
Thickness 0.492 - 0.984 in
 Temper T651; Standard EN 485-2
500 MPa

@Strain 0.200 %,
Thickness 25.0 - 60.0 mm
 72500 psi

@Strain 0.200 %,
Thickness 0.984 - 2.36 in
 Typical Strength
510 MPa

@Strain 0.200 %,
Thickness 9.90 - 25.0 mm
 74000 psi

@Strain 0.200 %,
Thickness 0.390 - 0.984 in
 Typical Strength
Elongation at Break >= 4.0 %

@Thickness 50.0 - 60.0 mm
 >= 4.0 %

@Thickness 1.97 - 2.36 in
 Temper T651; Standard EN 485-2
>= 4.0 %

@Thickness 60.0 - 80.0 mm
 >= 4.0 %

@Thickness 2.36 - 3.15 in
 Temper T651; Standard EN 485-2
>= 5.0 %

@Thickness 25.0 - 50.0 mm
 >= 5.0 %

@Thickness 0.984 - 1.97 in
 Temper T651; Standard EN 485-2
>= 6.0 %

@Thickness 12.5 - 25.0 mm
 >= 6.0 %

@Thickness 0.492 - 0.984 in
 Temper T651; Standard EN 485-2
>= 8.0 %

@Thickness 9.90 - 12.5 mm
 >= 8.0 %

@Thickness 0.390 - 0.492 in
 Temper T651; Standard EN 485-2
9.0 %

@Thickness 60.0 - 80.0 mm
 9.0 %

@Thickness 2.36 - 3.15 in
 Typical Elongation
10 %

@Thickness 9.90 - 25.0 mm
 10 %

@Thickness 0.390 - 0.984 in
 Typical Elongation
10 %

@Thickness 25.0 - 60.0 mm
 10 %

@Thickness 0.984 - 2.36 in
 Typical Elongation
Modulus of Elasticity 72.0 GPa
10400 ksi
Thermal Properties Metric English Comments
CTE, linear 23.6 µm/m-°C

@Temperature 20.0 - 100 °C
 13.1 µin/in-°F

@Temperature 68.0 - 212 °F
Thermal Conductivity 115 - 140 W/m-K
798 - 972 BTU-in/hr-ft²-°F
Temper T651
Component Elements Properties Metric English Comments
Aluminum, Al 87.32 - 91.42 %
87.32 - 91.42 %
as balance
Chromium, Cr 0.18 - 0.28 %
0.18 - 0.28 %
Copper, Cu 1.2 - 2.0 %
1.2 - 2.0 %
Iron, Fe <= 0.50 %
<= 0.50 %
Magnesium, Mg 2.1 - 2.9 %
2.1 - 2.9 %
Manganese, Mn <= 0.30 %
<= 0.30 %
Silicon, Si <= 0.40 %
<= 0.40 %
Zinc, Zn 5.1 - 6.1 %
5.1 - 6.1 %
Zr+Ti <= 0.20 %
<= 0.20 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.00000480 - 0.00000590 ohm-cm
0.00000480 - 0.00000590 ohm-cm
Temper T651