Chosun Refractories TCH-175SV Torpedo Castable
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Chosun Refractories TCH-175SV Torpedo Castable.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.004905 GPa <br>@Temperature 110 °C,<br> Time 86400 sec |
0.7114 ksi <br>@Temperature 230 °F,<br> Time 24.0 hour |
|
| 0.005886 GPa <br>@Temperature 1350 °C,<br> Time 10800 sec |
0.8537 ksi <br>@Temperature 2460 °F,<br> Time 3.00 hour |
||
| 0.007848 GPa <br>@Temperature 1500 °C,<br> Time 10800 sec |
1.138 ksi <br>@Temperature 2730 °F,<br> Time 3.00 hour |
||
| Compressive Strength | 19.6 MPa <br>@Temperature 110 °C,<br> Time 86400 sec |
2840 psi <br>@Temperature 230 °F,<br> Time 24.0 hour |
Cold Crushing Strength |
| 29.4 MPa <br>@Temperature 1350 °C,<br> Time 10800 sec |
4270 psi <br>@Temperature 2460 °F,<br> Time 3.00 hour |
Cold Crushing Strength | |
| 39.2 MPa <br>@Temperature 1500 °C,<br> Time 10800 sec |
5690 psi <br>@Temperature 2730 °F,<br> Time 3.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 1650 °C | 3000 °F | limited |
| Shrinkage | -0.150 % <br>@Temperature 1500 °C,<br> Time 10800 sec |
-0.150 % <br>@Temperature 2730 °F,<br> Time 3.00 hour |
|
| -0.0900 % <br>@Temperature 1350 °C,<br> Time 10800 sec |
-0.0900 % <br>@Temperature 2460 °F,<br> Time 3.00 hour |
||
| -0.0600 % <br>@Temperature 110 °C,<br> Time 86400 sec |
-0.0600 % <br>@Temperature 230 °F,<br> Time 24.0 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 75 % | 75 % | |
| SiC | 15 % | 15 % | |
| SiO2 | 5.0 % | 5.0 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Ramm,vibrating | |
| Material Required for Estimating(kg/?) | 2,600 |
Users viewing this material also viewed the following:
- Plasma Coatings 19000 Surface Material
- Plastcom SLOVALEN PC 69 GF 35 FRT 4 Polypropylene Copolymer, 35% Glass Fiber, Halogen Free and Phosphor Free Flame Retardant
- Cookson Group Plaskon® PPF-165A Molding Compound (discontinued **)
- LG Chemical LUCEL FW700S Modified POM, Friction Resistance, Abrasion Resistance
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR N990 Filler
- ExxonMobil Label-Lyte™ ROSO 50LR210 OPP Film
- Hippe PF CC 202 Woven Cotton Cloth Reinforced Phenolic Resin - Sheet
- 3M Scotchcast™ 5555 22G Electrical Insulating Epoxy Resin
- A. Schulman ComAlloy Hiloy® 630 Nylon 6/6, Glass/Mineral Reinforced, Flow Enhanced, UL
Copyright © lookpolymers.com All Rights Reserved