- HOME
- POLYMER SEARCH
- Oxide
- Aluminum Oxide
- Chosun Refractories SFC-UL90S High-Alumina Castable
Chosun Refractories SFC-UL90S High-Alumina Castable
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories SFC-UL90S High-Alumina Castable.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.00981 GPa @Temperature 110 °C, Time 86400 sec |
1.42 ksi @Temperature 230 °F, Time 24.0 hour |
|
| 0.024525 GPa @Temperature 1350 °C, Time 10800 sec |
3.5571 ksi @Temperature 2460 °F, Time 3.00 hour |
||
| 0.027468 GPa @Temperature 1400 °C, Time 10800 sec |
3.9840 ksi @Temperature 2550 °F, Time 3.00 hour |
||
| Compressive Strength | 63.7 MPa @Temperature 110 °C, Time 86400 sec |
9250 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| 93.2 MPa @Temperature 1350 °C, Time 10800 sec |
13500 psi @Temperature 2460 °F, Time 3.00 hour |
Cold Crushing Strength | |
| 108 MPa @Temperature 1400 °C, Time 10800 sec |
15600 psi @Temperature 2550 °F, Time 3.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 1800 °C | 3270 °F | limited |
| Shrinkage | -0.300 % @Temperature 1350 °C, Time 10800 sec |
-0.300 % @Temperature 2460 °F, Time 3.00 hour |
|
| -0.150 % @Temperature 1400 °C, Time 10800 sec |
-0.150 % @Temperature 2550 °F, Time 3.00 hour |
||
| -0.0300 % @Temperature 110 °C, Time 86400 sec |
-0.0300 % @Temperature 230 °F, Time 24.0 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 87 % | 87 % | |
| SiC | 5.0 % | 5.0 % | |
| SiO2 | 6.0 % | 6.0 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Self Flowing | |
| Material Required for Estimating(kg/?) | 3,200 | |
| Water Required for Casting(%) | 4.2-4.7 |
Users viewing this material also viewed the following:
- Radici Radilon® S CP400 (dry) Nylon 6
- Karina E 27/8-GIN Fume MBATCH (SP31452) for PVC
- Karina E 845-35/2-CRM Ivory PVC Compound
- A. Schulman POLYBATCH™ Orange LL10257/4 Concentrate Based In LLDPE
- Clariant Renol PCSP0010 Polycarbonate Alloy, Glass Fiber and Glass Bead Filled
- Dow Corning 200® 1.5 CST FLUID
- Axiall 7768 Rigid PVC, Extrusion
- 3A Composites Core Materials AIREX® PXc.385 Fiber-Reinforced Structural Foam
- EMS-Grivory Grivory® TS V0 X PA666 FR
- Henkel Hysol EA 9313 Paste Adhesive System
Copyright © lookpolymers.com All Rights Reserved