Chosun Refractories INCT-170 Light-Weight Castable
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories INCT-170 Light-Weight Castable.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 5.77e-7 - 0.00294 GPa @Temperature 110 °C, Time 86400 sec |
0.0000837 - 0.427 ksi @Temperature 230 °F, Time 24.0 hour |
|
| 0.0014715 - 0.0044145 GPa @Temperature 1350 °C, Time 10800 sec |
0.21343 - 0.64028 ksi @Temperature 2460 °F, Time 3.00 hour |
||
| 0.002943 - 0.005886 GPa @Temperature 1500 °C, Time 10800 sec |
0.4269 - 0.8537 ksi @Temperature 2730 °F, Time 3.00 hour |
||
| Compressive Strength | 4.90 - 14.7 MPa @Temperature 1350 °C, Time 10800 sec |
711 - 2130 psi @Temperature 2460 °F, Time 3.00 hour |
Cold Crushing Strength |
| 9.81 - 19.6 MPa @Temperature 1500 °C, Time 10800 sec |
1420 - 2840 psi @Temperature 2730 °F, Time 3.00 hour |
Cold Crushing Strength | |
| 9.81 - 19.6 MPa @Temperature 110 °C, Time 86400 sec |
1420 - 2840 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.8724 W/m-K @Temperature 1000 °C |
6.044 BTU-in/hr-ft²-°F @Temperature 1830 °F |
|
| Maximum Service Temperature, Air | 1700 °C | 3090 °F | limited |
| Shrinkage | -0.500 % @Temperature 1350 °C, Time 10800 sec |
-0.500 % @Temperature 2460 °F, Time 3.00 hour |
|
| -0.0300 % @Temperature 110 °C, Time 86400 sec |
-0.0300 % @Temperature 230 °F, Time 24.0 hour |
||
| 0.50 % @Temperature 1500 °C, Time 10800 sec |
0.50 % @Temperature 2730 °F, Time 3.00 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 92 % | 92 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Casting, Troweling | |
| Main Applications | Deoxidizing gas resistance High temp. | |
| Material Required for Estimating (kg/?) | 1,500 | |
| Water Required for Casting(%) | 15-20 |
Users viewing this material also viewed the following:
- Haynes 230® alloy, 40% cold reduction, 1177°C anneal for 5 minutes
- Garlock Klozure® Mill-Right® N NBR Oil Seal
- Solvay Technyl® C216V25 25% Glass Filled Nylon 6
- Solvay Specialty Polymers FOMBLIN® Z03 PFPE Lubricant
- Saint-Gobain CHR® 2965-8R Glass-Silicone Backing Silicone Adhesive Pressure Sensitive Tape
- Silberline SilBerCote® PC 8602X
- A. Schulman PP 1188-01 Polypropylene Extra High-Impact Polypropylene
- Eurotec® Tecodur® PB70 GR50 NL100 PBT, 50% glass fiber reinforced, natural
- Dynasol Calprene® 710 Thermoplastic Rubber SBS Dry
- 3M Scotch-Weld™ MG1500 PR Medical Grade Instant Adhesive
Copyright © lookpolymers.com All Rights Reserved