Chosun Refractories INCT-110N Light-Weight Castable
| Category | Ceramic , Oxide , Silicon Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories INCT-110N Light-Weight Castable.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 3.37e-7 - 0.00147 GPa @Temperature 110 °C, Time 86400 sec |
0.0000489 - 0.213 ksi @Temperature 230 °F, Time 24.0 hour |
|
| 0.0014715 - 0.0034335 GPa @Temperature 500 °C, Time 10800 sec |
0.21343 - 0.49799 ksi @Temperature 932 °F, Time 3.00 hour |
||
| Compressive Strength | 2.94 - 7.85 MPa @Temperature 1000 °C, Time 10800 sec |
427 - 1140 psi @Temperature 1830 °F, Time 3.00 hour |
Cold Crushing Strength |
| 4.90 - 9.81 MPa @Temperature 110 °C, Time 86400 sec |
711 - 1420 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength | |
| 4.90 - 9.81 MPa @Temperature 500 °C, Time 10800 sec |
711 - 1420 psi @Temperature 932 °F, Time 3.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.3024 W/m-K @Temperature 260 °C |
2.095 BTU-in/hr-ft²-°F @Temperature 500 °F |
|
| 0.3257 W/m-K @Temperature 540 °C |
2.257 BTU-in/hr-ft²-°F @Temperature 1000 °F |
||
| 0.41873 W/m-K @Temperature 800 °C |
2.9013 BTU-in/hr-ft²-°F @Temperature 1470 °F |
||
| Maximum Service Temperature, Air | 1100 °C | 2010 °F | limited |
| Shrinkage | -0.430 % @Temperature 1000 °C, Time 10800 sec |
-0.430 % @Temperature 1830 °F, Time 3.00 hour |
|
| -0.0600 % @Temperature 110 °C, Time 86400 sec |
-0.0600 % @Temperature 230 °F, Time 24.0 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 25 % | 25 % | |
| SiO2 | 55 % | 55 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Casting, Troweling | |
| Main Applications | Low temperature Various furnaces | |
| Material Required for Estimating (kg/?) | 1,150 | |
| Water Required for Casting(%) | 35-45 |
Users viewing this material also viewed the following:
- Solvay Engineered Polymers SEQUEL® 2300 Engineered Polyolefin (discontinued **)
- Polykemi AB POLYfill PPH Q15030 E10 Polypropylene Homopolymer, Mineral Reinforced, Elastomer Modified
- Polimeri Europa Edistir RK Polystyrene (discontinued **)
- Propylene Oxide Rubber (GPO)
- M Chemical GUARD DOGâ„¢ UV1577 Light Absorber, Triazene Derivative
- Dow Corning C6-560 LIQUID SILICONE RUBBER KIT
- Arlon 23234R025 0.025" (0.635 mm) Semi-Cured Silicone Rubber with Fiberglass Substrate
- C.O.I.M. LARIPUR® LPR6260 PTMG Polyether Polyurethane
- Advanced Polymer Alloys DURACRYN 8080 NC Thermoplastic Rubber
Copyright © lookpolymers.com All Rights Reserved