- Chosun Refractories GUN-110L Light-Weight Gunning Castable
Chosun Refractories GUN-110L Light-Weight Gunning Castable
| Category | Ceramic |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories GUN-110L Light-Weight Gunning Castable.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 1.92e-7 - 0.00118 GPa @Temperature 110 °C, Time 86400 sec |
0.0000279 - 0.171 ksi @Temperature 230 °F, Time 24.0 hour |
|
| 0.0006867 - 0.0014715 GPa @Temperature 1000 °C, Time 10800 sec |
0.09960 - 0.21343 ksi @Temperature 1830 °F, Time 3.00 hour |
||
| Compressive Strength | 1.47 - 2.94 MPa @Temperature 1000 °C, Time 10800 sec |
213 - 427 psi @Temperature 1830 °F, Time 3.00 hour |
Cold Crushing Strength |
| 2.45 - 3.92 MPa @Temperature 110 °C, Time 86400 sec |
356 - 569 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.2792 W/m-K @Temperature 260 °C |
1.934 BTU-in/hr-ft²-°F @Temperature 500 °F |
|
| 0.3024 W/m-K @Temperature 540 °C |
2.095 BTU-in/hr-ft²-°F @Temperature 1000 °F |
||
| 0.3257 W/m-K @Temperature 800 °C |
2.257 BTU-in/hr-ft²-°F @Temperature 1470 °F |
||
| Maximum Service Temperature, Air | 1100 °C | 2010 °F | limited |
| Shrinkage | -0.900 % @Temperature 1000 °C, Time 10800 sec |
-0.900 % @Temperature 1830 °F, Time 3.00 hour |
|
| -0.100 % @Temperature 110 °C, Time 86400 sec |
-0.100 % @Temperature 230 °F, Time 24.0 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 29 % | 29 % | |
| SiO2 | 39 % | 39 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Gunning | |
| Main Applications | General Uses | |
| Material Required for Estimating (kg/?) | 1,100 | |
| Water Required for Casting(%) | Nozzle Mixing |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-FLEX 602A Conductive Resin Blend
- PolyOne Lubri-Tech™ PI-10CF/15T Polyetherimide (PEI), Carbon Fiber Reinforced, PTFE Lubricated (discontinued
- Lehmann & Voss LUVOCOM® 50-7814/EM Polycarbonate, with glass fiber and PTFE
- Mearthane Durethaneâ„¢ M DM-640A Foam Polyurethane
- Lucite International Diakon® Rapide CLG 356B Enhanced Molding Acrylic Polymer
- Hexcel® HexPly® M47 140°C Curing Epoxy Matrix, Unidirectional Carbon Prepreg IM2-C Fibre
- Eagle Brass 18665 MSP1, Spring
- DSM Stanyl® TW250F6 Nylon 46-30% Glass Reinforced (European Grade) (Cond)
- DuPont Teijin Films Melinex® 457 Polyester Film, 200 Gauge
Copyright © lookpolymers.com All Rights Reserved