Chevron Phillips Ryton® PR09-60 Polyphenylene Sulfide Compound, Annealed 2 hours at 200°C (discontinued **)&l

Category	Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS); Molded
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Chevron Phillips Ryton® PR09-60 Polyphenylene Sulfide Compound, Annealed 2 hours at 200°C (discontinued **)&l.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Polyphenylene Sulfide CompoundRyton® PR09-60 Annealed 2 hours at 200°C is pelletized unfilled high molecular weight polyphenylene sulfide resin suitable for extrusion or injection molding.Comments: Test specimen molding conditions: Stock Temperature, 315-345°C; Mold Temperature, 135°C; ASTM Values Converted to SI UnitsData provided by Chevron Phillips Chemical Company LP.Solvay Specialty Polymers has acquired the Ryton product line. This product was discontinued prior to the acquisition and is listed under the Chevron Phillips name for historical purposes.

Physical Properties	Metric	English	Comments
Density	1.35 g/cc	0.0488 lb/in³	ASTM D792
Water Absorption	0.050 %	0.050 %	ASTM D570

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	85.0 MPa	12300 psi	ASTM D638
Elongation at Break	2.5 %	2.5 %	ASTM D638
Flexural Yield Strength	130 MPa	18900 psi	ASTM D790
Flexural Modulus	3.80 GPa	551 ksi	ASTM D790
Izod Impact, Unnotched	8.00 J/cm	15.0 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear	53.0 µm/m-°C @Temperature -50.0 - 50.0 °C	29.4 µin/in-°F @Temperature -58.0 - 122 °F	Axial; ASTM E831
Thermal Conductivity	0.300 W/m-K	2.08 BTU-in/hr-ft²-°F
Deflection Temperature at 1.8 MPa (264 psi)	120 °C	248 °F	ASTM D648
Flammability, UL94	V-0	V-0

Electrical Properties	Metric	English	Comments
Electrical Resistivity	1.00e+16 ohm-cm	1.00e+16 ohm-cm	ASTM D257
Surface Resistance	1.00e+12 ohm @Temperature 90.0 °C	1.00e+12 ohm @Temperature 194 °F	95% RH, 48 hrs
Dielectric Constant	3.1 @Frequency 1000 Hz	3.1 @Frequency 1000 Hz	ASTM D150
	3.1 @Frequency 1e+6 Hz	3.1 @Frequency 1e+6 Hz	ASTM D150
Dielectric Strength	24.0 kV/mm	610 kV/in	ASTM D149
Dissipation Factor	0.0020 @Frequency 1000 Hz	0.0020 @Frequency 1000 Hz	ASTM D150
	0.0020 @Frequency 1e+6 Hz	0.0020 @Frequency 1e+6 Hz	ASTM D150
Arc Resistance	50 sec	50 sec	ASTM D495
Comparative Tracking Index	150 V	150 V	UL 746A