Chevron Phillips HiD® 9502/HiD® 9503 with Antistat HDPE Blow Molding Resin (discontinued **)

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Chevron Phillips HiD® 9502/HiD® 9503 with Antistat HDPE Blow Molding Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Resin Type: Linear Copolymer; Blow Molding ResinCharacteristics: Medium Molecular Weight Distribution, Wide Range of Processing Conditions, Excellent ESCR, High Melt Strength, Good Impact Resistance, Good Parison Uniformity, Good TrimabilityApplications:Hard to Hold Chemicals, Household-Industrial Chemical Containers, Detergents. Burn Rate

Physical Properties	Metric	English	Comments
Density	0.946 g/cc	0.0342 lb/in³	ASTM D1505
Apparent Bulk Density	0.590 g/cc	0.0213 lb/in³	ASTM D1895
Melt Flow	0.27 g/10 min @Load 2.16 kg, Temperature 190 °C	0.27 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D 1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	65	65	ASTM D2240
Tensile Strength, Yield	27.6 MPa	4000 psi	ASTM D638
Elongation at Break	>= 500 %	>= 500 %	ASTM D638
Flexural Modulus	0.900 GPa	131 ksi	3 pt. secant. ASTM D790
Tensile Impact Strength	159 kJ/m²	75.7 ft-lb/in²	S Bar; ASTM D 1822

Thermal Properties	Metric	English	Comments
Vicat Softening Point	123 °C	253 °F	ASTM D1525
Brittleness Temperature	<= -75.0 °C	<= -103 °F	ASTM D746