Chesterton MRS 10 Metal Rebuilding System

Category	Ceramic
Manufacturer	Chesterton
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Chesterton MRS 10 Metal Rebuilding System.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: A reinforced composite for the repair and protection of metal surfaces. It is machinable with excellent compressive strength, chemical resistance It is non-sagging, non-shrinking and 100% solids. The MRS 10 is formulated for applications where machining to exact tolerance is required or desired. It is frequently used as an alternative to resurfacing by welding or flame spraying. MRS 10 is easily mixed and applied and cures without the need of heat or pressure. Benefits:High build characteristics allows for single coat applicationsTough resin structure resists thermal-mechanical shockOutstanding adhesion insures reliable performanceCan be easily machined to exact tolerance. Convenient 4-1 mix ratio and verification of mix by color changePerforms well under fluctuating chemical environmentsResists compression setting.Suggested Uses:CondensersCooling Water PumpsFlange FacesHydraulic RamsKeywaysValve BodiesBearing HousingsShaftsSpline RepairsPitted CastingsHeat ExchangersPump VolutesInformation provided by Chesterton

Physical Properties	Metric	English	Comments
Density	2.00 g/cc	0.0723 lb/in³	Cured

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	105	105	ASTM D785
Hardness, Shore D	86	86	ASTM D2240
Tensile Strength at Break	27.6 MPa	4000 psi	ASTM D638
Flexural Strength	68.9 MPa	10000 psi	ASTM D790
Flexural Modulus	3.52 GPa	510 ksi	ASTM D790
Compressive Strength	89.6 MPa	13000 psi	ASTM D695
Taber Abrasion, mg/1000 Cycles	275 @Load 0.250 kg	275 @Load 0.551 lb	H-18, loss; ASTM D4060

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	66.0 °C	151 °F	Wet
	93.0 °C	199 °F	Dry

Processing Properties	Metric	English	Comments
Cure Time	60.0 min @Temperature 32.0 °C	1.00 hour @Temperature 89.6 °F	Tack Free
	120 min @Temperature 25.0 °C	2.00 hour @Temperature 77.0 °F	Tack Free
	150 min @Temperature 32.0 °C	2.50 hour @Temperature 89.6 °F	Light Load
	180 min @Temperature 16.0 °C	3.00 hour @Temperature 60.8 °F	Tack Free
	210 min @Temperature 25.0 °C	3.50 hour @Temperature 77.0 °F	Light Load
	300 min @Temperature 10.0 °C	5.00 hour @Temperature 50.0 °F	Tack Free
	420 min @Temperature 16.0 °C	7.00 hour @Temperature 60.8 °F	Light Load
	540 min @Temperature 10.0 °C	9.00 hour @Temperature 50.0 °F	Light Load
	960 min @Temperature 32.0 °C	16.0 hour @Temperature 89.6 °F	Full Load
	1200 min @Temperature 25.0 °C	20.0 hour @Temperature 77.0 °F	Full Load
	1800 min @Temperature 32.0 °C	30.0 hour @Temperature 89.6 °F	Full Chemical
	2160 min @Temperature 16.0 °C	36.0 hour @Temperature 60.8 °F	Full Load
	2160 min @Temperature 25.0 °C	36.0 hour @Temperature 77.0 °F	Full Chemical
	2880 min @Temperature 10.0 °C	48.0 hour @Temperature 50.0 °F	Full Load
	4320 min @Temperature 16.0 °C	72.0 hour @Temperature 60.8 °F	Full Chemical
	5760 min @Temperature 10.0 °C	96.0 hour @Temperature 50.0 °F	Full Chemical

Descriptive Properties	Value	Comments
Color	Grey