Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
Manufacturer | Carlson |
Trade Name | |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Carlson C 800H Nickel-Iron-Chromium Alloy.pdf |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 7.94 g/cc | 0.287 lb/in³ |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | >= 448 MPa | >= 65000 psi | |
Tensile Strength, Ultimate | 378 MPa @Temperature 649 °C |
54800 psi @Temperature 1200 °F |
|
465 MPa @Temperature 427 °C |
67500 psi @Temperature 800 °F |
||
Tensile Strength, Yield | 93.1 MPa @Temperature 649 °C |
13500 psi @Temperature 1200 °F |
|
130 MPa @Temperature 427 °C |
18800 psi @Temperature 800 °F |
||
>= 172 MPa @Strain 0.200 % |
>= 25000 psi @Strain 0.200 % |
||
Elongation at Break | >= 30 % | >= 30 % | |
Rupture Strength | 5.52 MPa @Temperature 982 °C, Time 3.60e+8 sec |
801 psi @Temperature 1800 °F, Time 100000 hour |
|
6.89 MPa @Temperature 982 °C, Time 1.08e+8 sec |
999 psi @Temperature 1800 °F, Time 30000 hour |
||
8.27 MPa @Temperature 982 °C, Time 3.60e+7 sec |
1200 psi @Temperature 1800 °F, Time 10000 hour |
||
89.63 MPa @Temperature 649 °C, Time 3.60e+8 sec |
13000 psi @Temperature 1200 °F, Time 100000 hour |
||
103.42 MPa @Temperature 649 °C, Time 1.08e+8 sec |
15000 psi @Temperature 1200 °F, Time 30000 hour |
||
120.65 MPa @Temperature 649 °C, Time 1.08e+8 sec |
17499 psi @Temperature 1200 °F, Time 30000 hour |
||
Modulus of Elasticity | 197 GPa | 28500 ksi | |
132 GPa @Temperature 871 °C |
19200 ksi @Temperature 1600 °F |
||
169.9 GPa @Temperature 427 °C |
24640 ksi @Temperature 800 °F |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 18.4 µm/m-°C @Temperature 21.1 - 871 °C |
10.2 µin/in-°F @Temperature 70.0 - 1600 °F |
|
Melting Point | 1357 - 1385 °C | 2475 - 2525 °F | |
Solidus | 1357 °C | 2475 °F | |
Liquidus | 1385 °C | 2525 °F |
Component Elements Properties | Metric | English | Comments |
---|---|---|---|
Aluminum, Al | 0.15 - 0.60 % | 0.15 - 0.60 % | |
Carbon, C | 0.050 - 0.10 % | 0.050 - 0.10 % | |
Chromium, Cr | 19 - 23 % | 19 - 23 % | |
Copper, Cu | <= 0.75 % | <= 0.75 % | |
Iron, Fe | >= 39.5 % | >= 39.5 % | |
Manganese, Mn | <= 1.5 % | <= 1.5 % | |
Nickel, Ni | 30 - 35 % | 30 - 35 % | |
Silicon, Si | <= 1.0 % | <= 1.0 % | |
Sulfur, S | <= 0.015 % | <= 0.015 % | |
Titanium, Ti | 0.15 - 0.60 % | 0.15 - 0.60 % |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Magnetic Permeability | 1.014 | 1.014 | 200 Oersted |
Curie Temperature | -115 °C | -175 °F |