Braskem CP 286 Injection Molding Polypropylene Heterophasic Copolymer

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer
Manufacturer	Braskem
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Braskem CP 286 Injection Molding Polypropylene Heterophasic Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: CP 286 is a high melt flow rate, heterophasic copolymer, suitable for injection moulding applications and also as base resin for compound. The resin combines excellent stiffness with good impact resistance, even at sub-zero temperatures.Applications: Base resin for compounding; High impact resistance parts.Information provided by Braskem.

Physical Properties	Metric	English	Comments
Specific Gravity	0.895 g/cc	0.895 g/cc	ASTM D792
Melt Flow	18 g/10 min @Load 2.16 kg, Temperature 230 °C	18 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	58	58	ASTM D785
Tensile Strength, Yield	21.0 MPa	3050 psi	ASTM D638
Elongation at Yield	5.0 %	5.0 %	ASTM D638
Flexural Modulus, 1% Secant	1000 MPa	145000 psi	1% secant; ASTM D790A
Izod Impact, Notched	0.800 J/cm @Temperature -20.0 °C	1.50 ft-lb/in @Temperature -4.00 °F	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	103 °C	217 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	54.0 °C	129 °F	ASTM D648
Vicat Softening Point	143 °C	289 °F	10 N; ASTM D1525