Bhansali Engineering Abstron PT-45M ABS Antistatic Extrusion Grade
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | Bhansali Engineering |
| Trade Name | Abstron |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Bhansali Engineering Abstron PT-45M ABS Antistatic Extrusion Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Antistatic Cop Sleeves ApplicationInformation provided by Bhansali
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.045 g/cc | 0.03775 lb/in³ | ASTM D-792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D-955 |
| Melt Flow | 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
8.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D-1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 102 | 102 | ASTM D-785 |
| Tensile Strength, Yield | 38.2 MPa @Thickness 3.20 mm |
5550 psi @Thickness 0.126 in |
Type 1, 5 mm/min speed; ASTM D-638 |
| Flexural Yield Strength | 48.1 MPa @Thickness 6.40 mm |
6970 psi @Thickness 0.252 in |
ASTM D-790 |
| Flexural Modulus | 1.77 GPa @Thickness 6.40 mm |
256 ksi @Thickness 0.252 in |
ASTM D-790 |
| Izod Impact, Notched | 3.7255 J/cm @Thickness 6.40 mm |
6.9794 ft-lb/in @Thickness 0.252 in |
ASTM D-256 |
| 5.098 J/cm @Thickness 3.20 mm |
9.551 ft-lb/in @Thickness 0.126 in |
ASTM D-256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | Method A - Annealed; ASTM D-648 |
| Vicat Softening Point | 99.0 °C | 210 °F | Method B; ASTM D-1525 |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
UL-94 |
Users viewing this material also viewed the following:
- Oxford Polymers 15GF 15% Glass Fiber Reinforced Polybutylene Terephthalate (PBT)
- MV Labs ZR550 (NH4)2ZrF6 Ammonium hexafluorozirconate (Hf< 50 ppm)
- LG Chemical LS100 PVC
- Lucite International Diakon® Rapide CLG 356B Enhanced Molding Acrylic Polymer
- Haynes HR-120® alloy, solution heat-treated aged at 1400°F for 1000 hours
- Latrobe LSSâ„¢ A7 Mod. Wear-Resistant Tool Steel (ASTM A7 Mod.)
- SABIC Innovative Plastics ULTEM HU2310 PEI (Europe-Africa-Middle East)
- ExxonMobil Enmist EP 460
- BASF Ultramid® A3L HP PA66 (Dry)
- BCC Products BC 9060 Silicone RTV Rubber
Copyright © lookpolymers.com All Rights Reserved