BNZ Materials Transite HT Low Temperature Industrial Board

Category	Ceramic , Oxide
Manufacturer	BNZ Materials, Inc.
Trade Name	Transite
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BNZ Materials Transite HT Low Temperature Industrial Board.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

These non-asbestos, monolithic fiber cement industrial boards are used in environments up to 1000°F where high strength is the primary concern. These fiber cement boards are used in the foundry industry for flask liners, core, drying and carry plates, and induction furnace casings. Electrical applications include busbar supports, aluminum pot insulation, and electrode arm insulators.Information provided by BNZ Materials Inc.

Physical Properties	Metric	English	Comments
Density	1.60 g/cc	0.0579 lb/in³

Mechanical Properties	Metric	English	Comments
Modulus of Rupture	0.0190 GPa	2.76 ksi
Compressive Yield Strength	44.8 MPa @Strain 5.00 %	6500 psi @Strain 5.00 %
Compressive Strength	71.7 MPa	10400 psi	ultimate load

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.340 W/m-K @Temperature 121 °C	2.36 BTU-in/hr-ft²-°F @Temperature 250 °F
Shrinkage	0.85 % @Temperature 316 °C, Time 86400 sec	0.85 % @Temperature 600 °F, Time 24.0 hour	Length/width
	3.7 % @Temperature 316 °C, Time 86400 sec	3.7 % @Temperature 600 °F, Time 24.0 hour	Thickness

Electrical Properties	Metric	English	Comments
Volume Resistivity	7.10e+10 ohm-cm	7.10e+10 ohm-cm	ASTM D257
Dielectric Strength	1.38 kV/mm	35.0 kV/in	ASTM D495
Arc Resistance	260 sec	260 sec	ASTM D495

Processing Properties	Metric	English	Comments
Moisture Content	12 %	12 %