BASF Ultramid® B3EG10 BK00564 50% Glass Filled PA6 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® B3EG10 BK00564 50% Glass Filled PA6 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid B3EG10 BK00564 is a 50% glass fiber reinforced injection molding PA6 grade.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 |
| Water Absorption | 4.8 % | 4.8 % | ISO 62 |
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | 23°C/50% R.H.; ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 203 MPa | 29400 psi | 5mm/min; ISO 527 |
| Elongation at Break | 2.1 % | 2.1 % | 5mm/min; ISO 527 |
| Tensile Modulus | 15.0 GPa | 2180 ksi | 1mm/min; ISO 527 |
| Flexural Modulus | 14.5 GPa | 2100 ksi | ISO Data |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | ISO Test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10 K/min |
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C | 414 °F | ISO 75 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | BK00564 | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics EXTEM UH1016 TPI Blend
- NOVA Chemicals EPS 33MB Modified Expandable Polystyrene
- Johnson Matthey Yara 58-Y1 N2O Abatement Catalyst
- Solvay Specialty Polymers Ixef® 1022 Polyarylamide (PARA), 50% Glass Fiber (Dry)
- Solvay Specialty Polymers Galden® HT80 PFPE Heat Transfer Fluid
- SMAC CABLE® 2518S-10-08 Damping Material
- Trelleborg Commercial Neoprene® C653 Chloroprene
- Plenco 6500 Phenolic, Briquette, Transfer Molded
- DuPont Teijin Films Melinex® 513P Polyester Film, 650 Gauge
- Chesterton 660 Silicone Lubricant
Copyright © lookpolymers.com All Rights Reserved