BASF Ultramid® 8270 HS PA6 (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer	BASF
Trade Name	Ultramid®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® 8270 HS PA6 (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Ultramid 8270 HS is a thermally modified PA6 blow molding compound exhibiting exceptional toughness and melt strength ideally suited for blow molding, profile extrusion, and other applications requiring extra high melt viscosity. It exhibits excellent permeability and chemical resistance to oils, hydrocarbons and most solvents.

Physical Properties	Metric	English	Comments
Density	1.13 g/cc	0.0408 lb/in³	dry; ISO 1183
Water Absorption	1.6 %	1.6 %	24 hour; ISO Test
	9.2 %	9.2 %	beginning dry; ISO 62
Moisture Absorption at Equilibrium	2.6 %	2.6 %	beginning dry (23°C/50% R.H.); ISO 62
Viscosity Measurement	220	220	Formic Acid

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	46.0 MPa	6670 psi	50mm/min; ISO 527
	46.0 MPa	6670 psi	2 in/min; ASTM Test
	119 MPa @Temperature -40.0 °C	17300 psi @Temperature -40.0 °F	ISO Data
	119 MPa @Temperature -40.0 °C	17300 psi @Temperature -40.0 °F	ASTM Test
Flexural Strength	37.0 MPa	5370 psi	ASTM Test
	176 MPa @Temperature -40.0 °C	25500 psi @Temperature -40.0 °F	ASTM Test
Flexural Modulus	0.760 GPa	110 ksi	ASTM Test
Izod Impact, Notched	0.480 J/cm @Temperature -40.0 °C	0.899 ft-lb/in @Temperature -40.0 °F	ASTM Test
	NB @Thickness 3.17 mm	NB @Thickness 0.125 in	ASTM Test

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	10 K/min
	220 °C	428 °F	ASTM Test

Descriptive Properties	Value	Comments
Color	Natural
Commercial Status	Active America
Form	Pellets
Impact Modified	No
Primary Processing Technique	Blow Molding
Processing	Blow molding
	Injection Molding
Special characteristic	Heat stabilized or stable to heat
UL.UL-C	Yes