BASF Ultradur B 4300 G4 BK5110 20% Glass Filled PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultradur B |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultradur B 4300 G4 BK5110 20% Glass Filled PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultradur B 4300 G4 BK5110 is an easy flowing, pigmented black, injection molding PBT with 20% glass fiber reinforcement for rigid, tough, and dimensionally stable parts.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 |
| Water Absorption | 0.20 % | 0.20 % | 24 hour; ISO Test |
| 0.40 % | 0.40 % | ISO 62 | |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H.; ISO 62 |
| Viscosity Test | 110 cm³/g | 110 cm³/g | Viscosity number |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 107 MPa | 15500 psi | 5mm/min; ISO 527 |
| Elongation at Break | 3.5 % | 3.5 % | 5mm/min; ISO 527 |
| Flexural Modulus | 6.10 GPa | 885 ksi | ISO Data |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | ISO Test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 223 °C | 433 °F | 10 K/min |
| 223 °C | 433 °F | ASTM Test | |
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | ISO 75 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | BK5110 | |
| Commercial Status | North America and Europe | |
| Form | Pellets | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding | |
| Special characteristic | Heat stabilized or stable to heat | |
| Light stabilized or stable to light | ||
| Lubricant | ||
| U.V. stabilized or stable to weather |
Users viewing this material also viewed the following:
- PolyOne Lubri-Tech™ AT-15GF/10T Acetal-Copolymer, Glass Filled, PTFE Lubricated (discontinued **)
- DSM Akulon® K224-G3U (Cond.) 15% Glass Reinforced Nylon 6 (North America) (discontinued **)
- Hyosung Topilene J340F PP
- MetalTek MTEK CZ-100 Cast UNS N02100 Severe Corrosion and Heat Resistant Alloy
- Karina E 32/1-FC-LMP Orange Color Concentrate for PVC
- Samsung Cheil Industries Infino® WP-1069 PC/ABS, Unreinforced
- Solvay JAGUAR® C 162 Surfactant
- A. Schulman FORMION™ FI 394 Ionomer
Copyright © lookpolymers.com All Rights Reserved