BASF Elastollan C 88 A TPUR

Category	Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade
Manufacturer	BASF
Trade Name	Elastollan
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Elastollan C 88 A TPUR.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties and chemical resistance, outstanding wear resistance, high tear and tensile strength, good damping characteristics and a high resilience performance.Typical Applications: Spiral tubing, pneumatic tubing, round and v-belting, technical moldings, e.g. bushes, dust caps, seals, blow molding bellows, and mining screens.Note: Quoted results are from measurements on injection molded test platens, post tempered for 20 hours at 100°CInformation provided by BASF

Physical Properties	Metric	English	Comments
Density	1.19 g/cc	0.0430 lb/in³	ISO 1183-1-A

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	88	88	ISO 868
Hardness, Shore D	37	37	ISO 686
Tensile Strength	38.0 MPa	5510 psi	after storage in water at 80°C for 42 days; ISO 37
	50.0 MPa	7250 psi	ISO 37
	3.50 MPa @Strain 20.0 %	508 psi @Strain 20.0 %	ISO 37
	6.00 MPa @Strain 100 %	870 psi @Strain 100 %	ISO 37
	13.0 MPa @Strain 300 %	1890 psi @Strain 300 %	ISO 37
Elongation at Break	600 %	600 %	ISO 37
	650 %	650 %	after storage in water at 80°C for 42 days; ISO 37
Charpy Impact, Notched	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	DIN EN ISO 179
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	DIN EN ISO 179
Tear Strength	75.0 kN/m	428 pli	DIN ISO 34-1/Bb
Abrasion	30	30	[mm<sup>3</sup>; ISO 4649
Compression Set	25 % @Temperature 23.0 °C	25 % @Temperature 73.4 °F	ISO 815
	40 % @Temperature 70.0 °C	40 % @Temperature 158 °F	ISO 815

Processing Properties	Metric	English	Comments
Processing Temperature	160 - 220 °C	320 - 428 °F	Extrusion
Mold Temperature	20.0 - 70.0 °C	68.0 - 158 °F

Descriptive Properties	Value	Comments
Commercial Status	North America
Primary Processing Technique	Extrusion

Users viewing this material also viewed the following: