BASF Elastollan B 64 D TPUR

Category	Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade
Manufacturer	BASF
Trade Name	Elastollan
Port	Ningbo port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	BASF Elastollan B 64 D TPUR.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties, outstanding wear resistance, high tensile strength, good damping and resilience performance and superior low temperature flexibility.Typical Applications: Sport-shoe soles and accessories, ski-boot shells, technical moldings, e.g. seals, castor tyres and tubing.Note: Quoted results are from measurements on injection molded test platens, post tempered for 20 hours at 100°CInformation provided by BASF

Physical Properties	Metric	English	Comments
Density	1.24 g/cc	0.0448 lb/in³	ISO 1183-1-A

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	64	64	ISO 686
Tensile Strength	40.0 MPa	5800 psi	after storage in water at 80°C for 42 days; ISO 37
	55.0 MPa	7980 psi	ISO 37
	17.0 MPa <br>@Strain 20.0 %	2470 psi <br>@Strain 20.0 %	ISO 37
	19.0 MPa <br>@Strain 100 %	2760 psi <br>@Strain 100 %	ISO 37
	35.0 MPa <br>@Strain 300 %	5080 psi <br>@Strain 300 %	ISO 37
Elongation at Break	400 %	400 %	after storage in water at 80°C for 42 days; ISO 37
	450 %	450 %	ISO 37
Charpy Impact, Notched	0.800 J/cm² <br>@Temperature -30.0 °C	3.81 ft-lb/in² <br>@Temperature -22.0 °F	DIN EN ISO 179
	NB <br>@Temperature 23.0 °C	NB <br>@Temperature 73.4 °F	DIN EN ISO 179
Tear Strength	180 kN/m	1030 pli	DIN ISO 34-1/Bb
Abrasion	25	25	[mm<sup>3</sup>; ISO 4649
Compression Set	35 % <br>@Temperature 23.0 °C	35 % <br>@Temperature 73.4 °F	ISO 815
	50 % <br>@Temperature 70.0 °C	50 % <br>@Temperature 158 °F	ISO 815

Processing Properties	Metric	English	Comments
Processing Temperature	175 - 230 °C	347 - 446 °F	Injection molding
Mold Temperature	20.0 - 70.0 °C	68.0 - 158 °F

Descriptive Properties	Value	Comments
Commercial Status	North America
Primary Processing Technique	Injection molding