BASF Elastollan® 1190A10 Wire & Cable Grade Polyurethane Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP
Manufacturer BASF
Trade Name Elastollan®
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF BASF Elastollan® 1190A10 Wire & Cable Grade Polyurethane Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
As with all TPU products this grade must be dried prior to processing.Information provided by BASF Corporation.
Physical Properties Metric English Comments
Density 1.13 g/cc
<br>@Thickness 2.00 mm
 0.0408 lb/in³
<br>@Thickness 0.0787 in
 molded plaque, cured 20 hr at 100°C; ASTM D792
Mechanical Properties Metric English Comments
Hardness, Shore A 90
<br>@Thickness 2.00 mm
 90
<br>@Thickness 0.0787 in
 molded plaque, cured 20 hr at 100°C; ASTM D2240
Tensile Strength, Ultimate 55.0 MPa
<br>@Thickness 2.00 mm
 7980 psi
<br>@Thickness 0.0787 in
 molded plaque, cured 20 hr at 100°C; ASTM D412
Tensile Strength, Yield 9.00 MPa
<br>@Strain 100 %
 1310 psi
<br>@Strain 100 %
 ASTM D-412
25.0 MPa
<br>@Strain 300 %
 3630 psi
<br>@Strain 300 %
 0.76 mm (0.030 in) extruded sheet; ASTM D-412
Elongation at Break 500 %
500 %
on 0.030 in extruded sheet; ASTM D-412
Flexural Modulus 0.0500 GPa
<br>@Thickness 2.00 mm
 7.25 ksi
<br>@Thickness 0.0787 in
 molded plaque, cured 20 hr at 100°C; ASTM D790
Tear Strength 58.0 kN/m
<br>@Thickness 0.762 mm
 331 pli
<br>@Thickness 0.0300 in
 Split tear strength, extruded sheet; ASTM D-1938
Graves Tear Strength 114 kN/m
<br>@Thickness 0.762 mm
 650 pli
<br>@Thickness 0.0300 in
 extruded sheet; ASTM D624
Taber Abrasion, mg/1000 Cycles 30
<br>@Thickness 2.00 mm
 30
<br>@Thickness 0.0787 in
 H-18 wheel; ASTM D-1044; molded plaque, cured 20 hr at 100°C.
Compression Set 45 %
<br>@Temperature 70.0 °C
 45 %
<br>@Temperature 158 °F
 22 hr @ 70°C; ASTM D-395; 0.080 in molded plaque after curing 20 hrs at 100°C.
25 %
<br>@Thickness 2.00 mm
 25 %
<br>@Thickness 0.0787 in
 22 hr at 23°C; molded plaque, cured 20 hr at 100°C.; ASTM D395
Tensile Set 32 %
32 %
at 200% elongation per ASTM D-412 is on 0.030 in extruded sheet.
Thermal Properties Metric English Comments
Vicat Softening Point 110 °C
<br>@Thickness 2.00 mm
 230 °F
<br>@Thickness 0.0787 in
 molded plaque, cured 20 hr at 100°C; ASTM D1525
Glass Transition Temp, Tg -35.0 °C
-31.0 °F
Pellet sample