BASF Elastollan® 1185A10U Wire & Cable Grade Polyurethane Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP
Manufacturer BASF
Trade Name Elastollan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Elastollan® 1185A10U Wire & Cable Grade Polyurethane Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
As with all TPU products this grade must be dried prior to processing.Information provided by BASF Corporation.
Physical Properties Metric English Comments
Density 1.13 g/cc

@Thickness 2.00 mm
 0.0408 lb/in³

@Thickness 0.0787 in
 molded plaque, cured 20 hr at 100°C; ASTM D792
Mechanical Properties Metric English Comments
Hardness, Shore A 86

@Thickness 2.00 mm
 86

@Thickness 0.0787 in
 molded plaque, cured 20 hr at 100°C; ASTM D2240
Tensile Strength, Ultimate 52.0 MPa

@Thickness 2.00 mm
 7540 psi

@Thickness 0.0787 in
 molded plaque, cured 20 hr at 100°C; ASTM D412
Tensile Strength, Yield 7.60 MPa

@Strain 100 %
 1100 psi

@Strain 100 %
 ASTM D-412
19.0 MPa

@Strain 300 %
 2760 psi

@Strain 300 %
 0.76 mm (0.030 in) extruded sheet; ASTM D-412
Elongation at Break 570 %
570 %
on 0.030 in extruded sheet; ASTM D-412
Flexural Modulus 0.0430 GPa

@Thickness 2.00 mm
 6.24 ksi

@Thickness 0.0787 in
 molded plaque, cured 20 hr at 100°C; ASTM D790
Tear Strength 66.0 kN/m

@Thickness 0.760 mm
 377 pli

@Thickness 0.0299 in
 Split tear strength; extruded sheet; ASTM D-1938
Graves Tear Strength 88.0 kN/m

@Thickness 0.762 mm
 502 pli

@Thickness 0.0300 in
 extruded sheet; ASTM D624
Taber Abrasion, mg/1000 Cycles 25

@Thickness 2.00 mm
 25

@Thickness 0.0787 in
 H-18 wheel; ASTM D-1044; molded plaque, cured 20 hr at 100°C.
Compression Set 25 %
25 %
22 hr at 23°C per ASTM D-395; 2.0 mm (0.080 in) molded plaque, cured 20 hr at 100°C.
45 %

@Temperature 70.0 °C
 45 %

@Temperature 158 °F
 22 hr @ 70°C; ASTM D-395; 0.080 in molded plaque after curing 20 hrs at 100°C.
Tensile Set 32 %
32 %
at 200% elongation per ASTM D-412 is on 0.030 in extruded sheet.
Thermal Properties Metric English Comments
Vicat Softening Point 100 °C

@Thickness 2.00 mm
 212 °F

@Thickness 0.0787 in
 molded plaque, cured 20 hr at 100°C.; ASTM D1525
Glass Transition Temp, Tg -40.0 °C
-40.0 °F
Pellet sample