BASF Capron® B85ZP Nylon 6 (DAM) (America)  (discontinued **)

Category Polymer , Film , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Capron® B85ZP Nylon 6 (DAM) (America)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Not Impact modified.Information provided by BASF.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO Test
Water Absorption 1.6 %
1.6 %
24 hr; ISO Test
9.5 %
9.5 %
ISO Test
Moisture Absorption at Equilibrium 2.7 %
2.7 %
23°C/50% R.H.; ISO Test
Oxygen Transmission 40.3 cc-mm/m²-24hr-atm
102 cc-mil/100 in²-24hr-atm
ASTM Test
Nitrogen Transmission 14.0 cc-mm/m²-24hr-atm
35.6 cc-mil/100 in²-24hr-atm
ASTM Test
Carbon Dioxide Transmission 72.8 cc-mm/m²-24hr-atm
185 cc-mil/100 in²-24hr-atm
ASTM Test
Viscosity 3.15 cP
3.15 cP
96% Sulfuric Acid; ISO Test
3.2 cP
3.2 cP
95% Sulfuric Acid; ISO Test
3.4 cP
3.4 cP
98% Sulfuric Acid; ISO Test
85 cP
85 cP
Formic Acid Viscosity; ISO Test
Linear Mold Shrinkage 0.014 cm/cm
0.014 in/in
MD; ASTM Test
Mechanical Properties Metric English Comments
Hardness, Rockwell R 119
119
ASTM Test
Tensile Strength, Yield 80.0 MPa
11600 psi
50 mm/min; ISO Test
80.0 MPa
11600 psi
2 in/min; ASTM Test
Flexural Strength 100 MPa
14500 psi
ASTM Test
Flexural Modulus 2.62 GPa
380 ksi
ASTM Test
Izod Impact, Notched 0.450 J/cm
0.843 ft-lb/in
1/8 in; ASTM Test
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
10 K/min; ISO Test
220 °C
428 °F
ASTM Test
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
ASTM Test
Descriptive Properties Value Comments
Color Natural
Primary Processing Film Extrusion