Ashley Polymers Ashlene® 105 PBT Polyester
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Unreinforced, Molded |
| Manufacturer | Ashley Polymers |
| Trade Name | Ashlene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ashley Polymers Ashlene® 105 PBT Polyester.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A general purpose polyester with low shrinkage and good flow.Data provided by the manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ASTM D792 |
| Water Absorption | 0.080 % | 0.080 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | ASTM D638 |
| Elongation at Break | 125 % | 125 % | ASTM D638 |
| Flexural Modulus | 2.10 GPa | 305 ksi | ASTM D790 |
| Izod Impact, Notched | 0.430 J/cm | 0.806 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 49.0 °C | 120 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Polykemi AB SCANTEC PC S90R Polycarbonate
- Huntsman PE 1011 Film Extrusion Polyethylene (discontinued **)
- H.C. Starck Amperit® 782.2 Titanium Oxide (TiO2)
- Mitsubishi Xantar® SF 2220 Polycarbonate-20% Glass Reinforced
- Hardwire 3SX-4-12 Low Density Tape
- SABIC Innovative Plastics LNP LUBRICOMP IL004 PA 6/12
- CRP Technology Windform® XT 2.0 Polyamide-Carbon Fiber Composite
- Aremco Pyro-Tape™ 682-ER High Temperature Tape Single layer polyimide film with silicone adhesive
Copyright © lookpolymers.com All Rights Reserved