Ascend Performance Materials Vydyne® 909 Nylon 66/6, 25% Glass Reinforced, Ignition Resistant, Conditioned

Category Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 30% Glass Fiber Reinforced
Manufacturer Ascend Performance Materials (formerly Solutia)
Trade Name VYDYNE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ascend Performance Materials Vydyne® 909 Nylon 66/6, 25% Glass Reinforced, Ignition Resistant, Conditioned.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vydyne® 909 is halogenated, 25% glass-filled, flame-retardant PA66/6 copolymer with excellent strength and toughness. It is lubricated for machine feed and easy mold release and has an Underwriters Laboratories UL 94 flammability classification of V-0 at 0.4 mm (0.016”) thick.Availability:Asia PacificEuropeNorth AmericaAdditive:HalogenLubricantFeatures:Good Crack ResistanceGood Mold ReleaseGood ToughnessHalogenatedHigh RigidityHigh StrengthIgnition ResistanceLubricatedUses:AppliancesAutomotive ElectronicsBobbinsConnectorsElectrical HousingElectrical PartsElectrical/Electronic ApplicationsFastenersIndustrial ApplicationsLighting ApplicationsLiving HingesPrinted Circuit BoardsSwitchesAppearance: Natural ColorForms: PelletsProcessing Method: Injection MoldingInformation provided by Ascend
Physical Properties Metric English Comments
Specific Gravity 1.47 g/cc
1.47 g/cc
ISO 1183
Water Absorption 0.70 %
0.70 %
24 hrs; ISO 62
Moisture Absorption at Equilibrium 1.3 %
1.3 %
50%rh; ISO 62
Linear Mold Shrinkage 0.0040 cm/cm

@Thickness 2.00 mm
0.0040 in/in

@Thickness 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.010 cm/cm

@Thickness 2.00 mm
0.010 in/in

@Thickness 0.0787 in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 90.0 MPa
13100 psi
ISO 527-2
Elongation at Break 3.0 %
3.0 %
ISO 527-2
Tensile Modulus 7.10 GPa
1030 ksi
ISO 527-2
Flexural Strength 140 MPa
20300 psi
ISO 178
Flexural Modulus 5.00 GPa
725 ksi
ISO 178