- Asahi Kasei Thermylene® P-30TC-1156 Chemically Coupled Polypropylene Compound, 30% Talc Filled
Asahi Kasei Thermylene® P-30TC-1156 Chemically Coupled Polypropylene Compound, 30% Talc Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Talc Filler |
| Manufacturer | Asahi Kasei |
| Trade Name | Thermylene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Thermylene® P-30TC-1156 Chemically Coupled Polypropylene Compound, 30% Talc Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive: Blower Wheels, HVAC Electrical and Specialty: Flush Valves, Pump BasesInformation provided by Asahi Kasei
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 12 g/10 min | 12 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 33.1 MPa | 4800 psi | |
| Elongation at Yield | 25 % | 25 % | |
| Flexural Modulus | 3.17 GPa | 460 ksi | |
| Izod Impact, Notched | 0.219 J/cm | 0.410 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 136.7 °C | 278.1 °F | |
| Flammability, UL94 | HB | HB |
Users viewing this material also viewed the following:
- Propex Fabrics Curv™ C100A Polypropylene/Polypropylene Thermoformable Composite
- M Chemical GUARD DOGâ„¢ UV292 HALS Light Stabilizer
- Micropol Microlin ML53 Linear Polyethylene Rotational Molding Powder
- Momentive Performance Materials N-Sil® RTV122 Silicone Modified Alkoxy Adhesive Sealants, White
- SABIC Innovative Plastics LNP LUBRICOMP KL004U Acetal Copolymer
- Dow Corning LSPBK 22 SILICONE MASTERBATCH
- Crucible Steel CPM® 1V® High Alloy Tool Steel
- 3M HGS8000X Glass Bubbles
- DuPont Performance Polymers Hytrel® 7246 TPC-ET (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved