Armstrong A-1/E Epoxy Adhesive

Category	Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer	Armstrong Epoxy Adhesives; Resin Technology Group
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Armstrong A-1/E Epoxy Adhesive.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

A brown epoxy paste formulated with enhanced wetting capabilities to hard rubbers and rigid thermoplastics. Has low outgassing characteristics at temperatures below 250°FInformation provided by Ellsworth Adhesives.

Physical Properties	Metric	English	Comments
Viscosity	400000 cP	400000 cP	Mixed

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	86	86
Tensile Strength, Ultimate	38.6 MPa	5600 psi	after optimum cure
Elongation at Break	1.4 %	1.4 %
Adhesive Bond Strength	40.7 MPa	5900 psi	Steel-Steel; after optimum cure
	18.3 MPa @Temperature -54.4 °C	2650 psi @Temperature -66.0 °F	Aluminum-Aluminum tensile shear
	19.3 MPa @Temperature 25.0 °C	2800 psi @Temperature 77.0 °F	Aluminum-Aluminum tensile shear
	19.3 MPa @Temperature 82.2 °C	2800 psi @Temperature 180 °F	Aluminum-Aluminum tensile shear

Thermal Properties	Metric	English
CTE, linear	24.0 µm/m-°C @Temperature 20.0 °C	13.3 µin/in-°F @Temperature 68.0 °F
Maximum Service Temperature, Air	121 °C	250 °F
Glass Transition Temp, Tg	111 °C	232 °F

Processing Properties	Metric	English	Comments
Processing Temperature	93.3 °C	200 °F	Optimum cure is 1 hr. @ 200°F
Pot Life	120 - 180 min @Temperature 25.0 °C	120 - 180 min @Temperature 77.0 °F	100 g

Descriptive Properties	Value	Comments
Color	Brown
Mix Ratio	100/6	By Weight