Arlon Thermavac® 0.060" (1.524 mm) Cured Silicone Vacuum Bagging (10502R060)

Category	Polymer , Thermoset , Silicone
Manufacturer	Arlon
Trade Name	Thermavac®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon Thermavac® 0.060" (1.524 mm) Cured Silicone Vacuum Bagging (10502R060).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Unsupported cured/post cured silicone rubber with a thickness of 0.060 in. ±0.006 (1.5 mm ±0.15); 0.003 in. (0.8 mm) polyethylene interleave. The shelf life is defined as the duration of time for which the product will meet the physical requirements outlined below. It does not guarantee the product’s usefulness in all applications. Color: Red. Weight: 2339 g/m² ± 234 (69.0 oz./yd.² ± 6.9).Applications: Composite vacuum bagging materials.Information provided by the manufacturer, Arlon Silicone Technologies Division.

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	50 - 60	50 - 60
Tensile Strength, Ultimate	7.47 - 9.13 MPa	1080 - 1320 psi
Elongation at Break	540 - 660 %	540 - 660 %
100% Modulus	0.00172 GPa	0.249 ksi	Average
Tear Strength	>= 43.8 kN/m	>= 250 pli
Compression Set	28 %	28 %	after post cure

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	232 °C	450 °F
Minimum Service Temperature, Air	-56.6 °C	-69.9 °F

Electrical Properties	Metric	English	Comments
Dielectric Strength	>= 15.75 kV/mm	>= 400.0 kV/in