Arkema Group Rilsan® AMN P20 TLD Nylon 12, Flexible, Injection Grade (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer Arkema
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Arkema Group Rilsan® AMN P20 TLD Nylon 12, Flexible, Injection Grade (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Designation ISO 1874-PA12-P,MHLR,14-005Flexible grade for injection molding. Available colors: black and natural. Light and heat stabilized. Mold-release agent.Good impact strength. Flexibility and dynamic properties. Easy filling of the mold due to its well adapted viscosity. Low shrinkage: include 1% on average for the design of the mold. Good dimensional stability (low moisture absorption).Example applications: Flexible parts with high impact strength and vibration resistance.ISO data provided by the manufacturer, Arkema.
Physical Properties Metric English Comments
Density 1.02 g/cc
0.0368 lb/in³
Water Absorption 1.4 %
1.4 %
Melt Flow 42 g/10 min

@Load 2.16 kg,
Temperature 235 °C
42 g/10 min

@Load 4.76 lb,
Temperature 455 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 31.0 MPa
4500 psi
50 mm/min
Elongation at Break >= 50 %
>= 50 %
Nominal Strain; 50 mm/min
Elongation at Yield 20 %
20 %
50 mm/min
Tensile Modulus 0.620 GPa
89.9 ksi
1 mm/min
Charpy Impact Unnotched NB
NB
NB
NB
Low Temp
Charpy Impact, Notched 0.880 J/cm²
4.19 ft-lb/in²
0.380 J/cm²

@Temperature -30.0 °C
1.81 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
Melting Point 174 °C
345 °F
10°C/min
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.10 mm
HB

@Thickness 0.122 in
Electrical Properties Metric English Comments
Dissipation Factor 0.000364

@Frequency 1e+6 Hz
0.000364

@Frequency 1e+6 Hz
0.000742

@Frequency 100 Hz
0.000742

@Frequency 100 Hz