Arkema Group Pebax® Rnew 70R53 SP 01 Polyether Block Amide (PEBA)

Category	Polymer , Renewable/Recycled Polymer , Thermoplastic , Polyether Block Amide (PEBA)
Manufacturer	Arkema
Trade Name	Pebax®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Pebax® Rnew 70R53 SP 01 Polyether Block Amide (PEBA).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Polyether block amide Pebax® 70R53 SP 01 is a thermoplastic elastomer made of flexible polyether and rigid polyamide based on renewable resources. This SP grade has been developed to be heat and UV resistant.Information provided by Arkema Group

Physical Properties	Metric	English	Comments
Density	1.03 g/cc	0.0372 lb/in³	ISO 1183
Water Absorption	1.0 % @Temperature 23.0 °C, Time 86400 sec	1.0 % @Temperature 73.4 °F, Time 24.0 hour	ISO 62
Moisture Absorption at Equilibrium	0.70 % @Temperature 20.0 °C	0.70 % @Temperature 68.0 °F	50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.013 cm/cm @Thickness 4.00 mm, Time 86400 sec	0.013 in/in @Thickness 0.157 in, Time 24.0 hour
Linear Mold Shrinkage, Transverse	0.012 cm/cm @Thickness 4.00 mm, Time 86400 sec	0.012 in/in @Thickness 0.157 in, Time 24.0 hour

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	70	70	Instantaneous, Conditioned 15 days at 23°C - 50% RH; ISO 868
	62 @Time 15.0 sec	62 @Time 0.00417 hour	Conditioned 15 days at 23°C - 50% RH; ISO 868
Tensile Strength at Break	57.0 MPa	8270 psi	Conditioned 15 days at 23°C - 50% RH; ASTM D638
Elongation at Break	>= 350 %	>= 350 %	Conditioned 15 days at 23°C - 50% RH; ASTM D638
Flexural Modulus	0.360 GPa	52.2 ksi	Conditioned 15 days at 23°C - 50% RH; ISO178
Charpy Impact Unnotched	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179
Charpy Impact, Notched	1.50 J/cm² @Temperature -30.0 °C	7.14 ft-lb/in² @Temperature -22.0 °F	ISO 179
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	186 °C	367 °F	ISO 11357
Vicat Softening Point	175 °C @Load 1.02 kg	347 °F @Load 2.25 lb	ISO 306

Component Elements Properties	Metric	English	Comments
Carbon, C	87 - 91 %	87 - 91 %	Renewable; ASTM 6866

Processing Properties	Metric	English	Comments
Processing Temperature	235 °C	455 °F	Recommended Extrusion Temperature
	220 - 250 °C	428 - 482 °F	Extrusion Range
Nozzle Temperature	230 - 290 °C	446 - 554 °F
	260 °C	500 °F	Recommended
Mold Temperature	25.0 - 60.0 °C	77.0 - 140 °F
Drying Temperature	70.0 - 80.0 °C	158 - 176 °F
Dry Time	5.00 - 7.00 hour	5.00 - 7.00 hour