Arkema Group Pebax® 5533 SN 01 Polyether Block Amide (PEBA) (Dry)

Category	Polymer , Thermoplastic , Elastomer, TPE , Polyether Block Amide (PEBA)
Manufacturer	Arkema
Trade Name	Pebax®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Pebax® 5533 SN 01 Polyether Block Amide (PEBA) (Dry).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

POLYETHER BLOCK AMIDE(PEBA) hardness 55 shore D Non plasticized flexible Polyamide Outstanding mechanical properties at low temperature (-40°C) Applications: overmolded parts for sport good (Football shoe sole) Industrial (conveyor belts, transmission belts)ISO data provided by the manufacturer, Arkema.

Physical Properties	Metric	English	Comments
Density	1.01 g/cc	0.0365 lb/in³
Water Absorption	1.2 %	1.2 %
Moisture Absorption at Equilibrium	0.50 %	0.50 %	Humidity Absorption
Melt Flow	8.0 g/10 min @Load 1.00 kg, Temperature 235 °C	8.0 g/10 min @Load 2.20 lb, Temperature 455 °F

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	55	55
Tensile Strength, Yield	12.0 MPa	1740 psi	50 mm/min
Elongation at Break	>= 50 %	>= 50 %	Nominal Strain; 50 mm/min
Elongation at Yield	32 %	32 %	50 mm/min
Tensile Modulus	0.156 GPa	22.6 ksi	1 mm/min
Charpy Impact Unnotched	NB	NB
	NB	NB	Low Temp
Charpy Impact, Notched	NB	NB
	NB	NB	Low Temp

Thermal Properties	Metric	English	Comments
Melting Point	159 °C	318 °F	10°C/min
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in

Optical Properties	Metric	English	Comments
Transmission, Visible	80 %	80 %	Mfr. reports 'Transparent' but doesn't quantify.

Electrical Properties	Metric	English
Electrical Resistivity	3.20e+13 ohm-cm	3.20e+13 ohm-cm
Surface Resistance	1.64e+13 ohm	1.64e+13 ohm
Dielectric Strength	38.5 kV/mm	978 kV/in
Dissipation Factor	0.00048 @Frequency 1e+6 Hz	0.00048 @Frequency 1e+6 Hz
	0.000943 @Frequency 100 Hz	0.000943 @Frequency 100 Hz
Comparative Tracking Index	600 V	600 V