- Arkema Group Orgalloy® RS 6620 Polyamide 6.6 Alloy 20% Glass Fiber reinforced
Arkema Group Orgalloy® RS 6620 Polyamide 6.6 Alloy 20% Glass Fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | Arkema |
| Trade Name | Orgalloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Orgalloy® RS 6620 Polyamide 6.6 Alloy 20% Glass Fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide Alloy, Rigid grade, Nylon 6.6 basedMolding of Engineering PartsInformation provided by Arkema Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO R1183 |
| Water Absorption | 0.50 % | 0.50 % | 23°C / 24 hrs; ISO 62 |
| Moisture Absorption at Equilibrium | 1.2 % | 1.2 % | 23°C / 50% RH; ISO 62 |
| 3.0 % | 3.0 % | in 23°C water; ISO 62 | |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 235 °C |
10 g/10 min @Load 4.76 lb, Temperature 455 °F |
after drying; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 82 | 82 | ISO 868 |
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | ISO R527 |
| Elongation at Break | 4.5 % | 4.5 % | ISO R527 |
| Modulus of Elasticity | 5.50 GPa | 798 ksi | ISO R527 |
| Flexural Strength | 160 MPa | 23200 psi | After conditioning at 23°C and 50% RH; ISO 178 |
| Flexural Modulus | 5.15 GPa | 747 ksi | After conditioning at 23°C and 50% RH; ISO 178 |
| Charpy Impact, Notched | 1.60 J/cm² | 7.61 ft-lb/in² | After conditioning at 23°C/50%RH; ISO 179/Af |
| 10.0 J/cm² @Temperature -20.0 °C |
47.6 ft-lb/in² @Temperature -4.00 °F |
After conditioning at 23°C/50%RH; ISO 179/Af | |
| Tensile Creep Modulus, 1 hour | 4900 MPa | 711000 psi | ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 35.0 µm/m-°C @Temperature 20.0 - 60.0 °C |
19.4 µin/in-°F @Temperature 68.0 - 140 °F |
TMS2 Perkin Elmer |
| CTE, linear, Transverse to Flow | 110 µm/m-°C @Temperature 20.0 - 60.0 °C |
61.1 µin/in-°F @Temperature 68.0 - 140 °F |
TMS2 Perkin Elmer |
| Melting Point | 255 °C | 491 °F | ISO R1218 |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ISO R75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO R75 |
| Vicat Softening Point | 160 °C | 320 °F | 50 N - B method; ISO 306 |
| >= 210 °C | >= 410 °F | 10 N - A method; ISO 306 | |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.10e+15 ohm-cm | 4.10e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 7.20e+15 ohm | 7.20e+15 ohm | ASTM D257 |
| Dielectric Strength | 36.0 kV/mm @Thickness 1.00 mm |
914 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Dissipation Factor | 0.017 @Frequency 100000 Hz |
0.017 @Frequency 100000 Hz |
NFC 26 230 |
| 0.028 @Frequency 100 Hz |
0.028 @Frequency 100 Hz |
NFC 26 230 | |
| 0.031 @Frequency 1000 Hz |
0.031 @Frequency 1000 Hz |
NFC 26 230 | |
| Comparative Tracking Index | >= 600 V | >= 600 V | NFC 26 220 |
Users viewing this material also viewed the following:
- Orion Engineered Carbons PRINTEX® L6 Beads Conductive Carbon Black
- STAR Thermoplastic Alloys & Rubbers StarTUFF TF 55-HR-9 TPE
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with DOP Plasticizer
- A. Schulman POLYBATCH™ Grey LL80316/3 Concentrate Based In LLDPE
- Tra-Con Supertherm 826M01 High Performance Diamond Epoxy Adhesive
- Fainplast Compounds FR 70/1 Flexible PVC, Insulation
- Aclo Accutech Polypropylene Copolymer CP0437M30CL Mica Reinforced Coupled
Copyright © lookpolymers.com All Rights Reserved