Arkema Group BONDINE® HX 8290 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride

Category	Polymer , Thermoplastic , EMAAA Terpolymer
Manufacturer	Arkema
Trade Name	BONDINE®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group BONDINE® HX 8290 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

BONDINE® HX 8290 is a random terpolymer of Ethylene, Acrylic Ester and Maleic Anhydride, polymerized under high pressure in an autoclave process. This grade is characterised by a high fluidity. Due to its properties (reactivity, fluidity), BONDINE® HX 8290 is an additive of choice for hot melt adhesives formulationInformation provided by Arkema Group

Physical Properties	Metric	English	Comments
Density	0.940 g/cc @Temperature 23.0 °C	0.0340 lb/in³ @Temperature 73.4 °F	ISO 1183
Melt Index of Compound	70 g/10 min @Load 2.16 kg, Temperature 190 °C	70 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	80	80	ASTM D2240
Tensile Strength at Break	5.60 MPa	812 psi	ASTM D638
Elongation at Break	500 %	500 %	ASTM D638
Flexural Modulus	0.0300 GPa	4.35 ksi	ASTM D638

Thermal Properties	Metric	English	Comments
Melting Point	85.0 °C	185 °F	DSC
Vicat Softening Point	<= 40.0 °C @Load 0.999 kg	<= 104 °F @Load 2.20 lb	ASTM D1525

Descriptive Properties	Value	Comments
Ethyl Acrylate Content (%)	17	IRTF (internal)
Maleic Anhydride Content (%)	2.8	IRTF (internal)