- Aremco Ceramabond™ 671 High Temperature Ceramic Adhesive/Paste, Alumina Filled
Aremco Ceramabond™ 671 High Temperature Ceramic Adhesive/Paste, Alumina Filled
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Aremco |
| Trade Name | Ceramabond™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aremco Ceramabond™ 671 High Temperature Ceramic Adhesive/Paste, Alumina Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Aremco's ceramic adhesives are easy to use, one- and two-component systems which air dry in 1-2 hrs and are ready for use following a 200 to 700 °F cure. These materials are mostly water-based and do not outgas after curing. They are also environmentally safe, non-flammable materials which contain no volatile organic compounds.General Features: High Adhesive Strength Bonding: Ceramic to Ceramic, Ceramic to Metal, Metal to Metal Principal Use: Textiles, Threadlocking
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.05 - 2.15 g/cc | 0.0741 - 0.0777 lb/in³ | |
| Volatile Organic Compounds (VOC) Content | 0.000 g/l | 0.000 g/l | |
| Viscosity | 40000 - 80000 cP | 40000 - 80000 cP |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Impact Test | 77.3 J | 57.0 ft-lb | Torque Strength; curing at 1000°F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 7.74 µm/m-°C | 4.30 µin/in-°F | |
| Maximum Service Temperature, Air | 1760 °C | 3200 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 7.17 kV/mm | 182 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 50.0 - 90.0 °C | 122 - 194 °F | Application Temp |
| Cure Time | 120 min @Temperature 93.3 °C |
2.00 hour @Temperature 200 °F |
preceeded by 1-4 hour air set |
| Shelf Life | 6.00 Month @Temperature 4.44 - 32.2 °C |
6.00 Month @Temperature 40.0 - 90.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Acid Resistance | Good | after curing at 700°F for 2 hours |
| Alkali Resistance | Excellent | after curing at 700°F for 2 hours |
| Color | White | |
| Moisture Resistance | Excellent | after curing at 700°F for 2 hours |
| Solvent | Water | |
| Thinner | 671-T |
Users viewing this material also viewed the following:
- Qualchem Danamid AFGFS2HUV14 Polyamide 66, 14% Glass Fiber
- Phillips 66 COPYLENE® CM010G Polypropylene Impact Copolymer
- LG Chemical LUMID LW4403B(W) PA66+GF/MF40%, Low Warpage
- Saint-Gobain Norton® T-100 Virgin Skived PTFE Film (0.005" thick)
- Silberline Sparkle Silver Ultraâ„¢ 6605
- Cossa Polimeri ESTAPROP KUR 0550 V0 HF Flame Retardant Polypropylene
- Eurostar Staramide RF004XXC PA6, 20% Glass Fiber Filled, Injection Molded
- DuPont Teijin Films Mylar® ADS Polyester Film, 300 Gauge
Copyright © lookpolymers.com All Rights Reserved