ArcelorMittal FB 450 Hot rolled ferrite-bainite steel

Category	Metal , Ferrous Metal , Alloy Steel
Manufacturer	ArcelorMittal
Trade Name	FB
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ArcelorMittal FB 450 Hot rolled ferrite-bainite steel.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Available in the following: uncoated (HDT450F) and Extragal® (HDT450F+Z)Description: This range of hot-rolled high strength steels has been developed to meet weight reduction requirements. It comprises four strength levels: FB 450, 540, 560 and 590. This family of steels extends the HSLA range of micro-alloyed steels to include products combining high tensile strength (UTS) with excellent formability and hole expansion (stretch flangeability) based on their ferrite-bainite microstructure.Applications: These steels are cold-drawn. The main applications are:structural parts (longitudinal beams, cross beams, car-body and ground liason parts),wheels,mechanical parts (ground liason parts, gear boxes...).ArcelorMittal has an extensive database relating to the forming and service properties of the entire range of ferrite-bainite steels. To integrate these steels at the design stage, a team of experts is available to perform specific studies based on modeling or laboratory tests.Information provided by ArcelorMittal

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	450 - 510 MPa	65300 - 74000 psi
Tensile Strength, Yield	300 - 380 MPa	43500 - 55100 psi
Elongation at Break	>= 25 %	>= 25 %	L<Sub>0</sub>=80 mm, th<3 mm
	>= 32 %	>= 32 %	L<Sub>0</sub>=5.65v <Sub>0</sub> mm, th<3 mm
Fatigue Strength	<= 320 MPa @# of Cycles 2.00e+6	<= 46400 psi @# of Cycles 2.00e+6
	<= 320 MPa @# of Cycles 1.00e+7	<= 46400 psi @# of Cycles 1.00e+7
	<= 400 MPa @# of Cycles 100000	<= 58000 psi @# of Cycles 100000

Component Elements Properties	Metric	English	Comments
Carbon, C	<= 0.17 %	<= 0.17 %
Iron, Fe	>= 98.98 %	>= 98.98 %	as balance
Manganese, Mn	<= 0.80 %	<= 0.80 %
Silicon, Si	<= 0.050 %	<= 0.050 %