Amity Thermosets ATS 766 Phenolic Molding Chopped cotton fabric Filler, Compression Molded

Category	Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic
Manufacturer	Amity Thermosets
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Amity Thermosets ATS 766 Phenolic Molding Chopped cotton fabric Filler, Compression Molded.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Characteristics:High impact strengthGlossy surfaceLow shrinkageGood sliding propertiesColor-BrownMedium flowApplications:Cog wheelsCastor wheelsBush bearingsPulleysWelding rod handlesTextile bobbins etc.Information provided by Amity Thermosets Limited

Physical Properties	Metric	English	Comments
Density	1.38 - 1.46 g/cc	0.0499 - 0.0527 lb/in³	Molding; IS 867-1963
Water Absorption	0.60 - 1.0 %	0.60 - 1.0 %	IS 13411-1993
Linear Mold Shrinkage	0.0032 - 0.0049 cm/cm	0.0032 - 0.0049 in/in	IS 13411-1992

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	>= 35.0 MPa	>= 5080 psi	5 mm/min.; IS 867-1963
Shear Strength	>= 56.0 MPa	>= 8120 psi	2mm/min.; IS 867-1963
Izod Impact, Notched	>= 1.55 J/cm	>= 2.90 ft-lb/in	IS 13411-1992

Processing Properties	Metric	English	Comments
Mold Temperature	160 - 170 °C	320 - 338 °F
Injection Pressure	15.68 - 34.3 MPa	2274 - 4970 psi	Mold Pressure
Cure Time	0.333 - 0.500 min	0.00556 - 0.00833 hour	per mm
Shelf Life	12.0 Month	12.0 Month