- Dow Corning MOLYKOTE® G-0052 FG WHITE EP BEARING GREASE
Dow Corning MOLYKOTE® G-0052 FG WHITE EP BEARING GREASE
| Category | Fluid , Lubricant |
| Manufacturer | Dow Corning |
| Trade Name | MOLYKOTE® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow Corning MOLYKOTE® G-0052 FG WHITE EP BEARING GREASE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Aluminum complex-thickened mineral oil food grade greaseInformation provided by Dow Corning
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.890 g/cc @Temperature 25.0 °C |
0.890 g/cc @Temperature 77.0 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Four Ball Extreme Pressure, Weld Load | 299.7 kg | 660.8 lb (mass) | |
| Penetration P(0), 1/10 mm | 280 | 280 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 150 °C | 302 °F | |
| Minimum Service Temperature, Air | -12.0 °C | 10.4 °F | |
| Dropping Point | 246 °C | 475 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Shelf Life | 60.0 Month | 60.0 Month |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | white | |
| NLGI Number | 2 |
Users viewing this material also viewed the following:
- Quadrant EPP Techtron® PSBG PPS, Polyphenylene sulfide, bearing grade, compression molded (ASTM Product Data Sheet)
- Resinoid 2225 Phenolic Molding, Cellulose Reinforced
- Haynes 625 alloy, plate, as annealed at 1025°C, rapid cooled
- Techmer ES HiFill® PA4/6 GF33 HS NAT 33% Glass Filled (Conditioned)
- Washington Penn Medium Impact Copolymer
- Eagle Brass 316L Austenitic Stainless Steel, 3/4 Hardened
- EMS-Grivory Grivory® GVS-5H black 9915 PA*-GF50
- Ascend Performance Materials Vydyne® R535 Nylon 66, 35% Glass Reinforced, DAM
- Lanxess Pocan® B 3235 XF 000000 PBT, 30% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved