Amity Thermosets ATR 126 Phenolic Molding Organic Filler, Compression Molded

Category	Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic
Manufacturer	Amity Thermosets
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Amity Thermosets ATR 126 Phenolic Molding Organic Filler, Compression Molded.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Characteristics:Ammonia freeGood mouldabilityGood mechanical strengthGood electrical insulationGood surface finishMedium thermal stability Color-black, brownSoft/medium flow Applications:Telecommunication equipment partsAutomotive electrical parts Moulding which remain in contact with metal partsElectric switchgear components ( eg. relay )Components exposed to warm atmosphere, etc. Information provided by Amity Thermosets Limited

Physical Properties	Metric	English	Comments
Density	1.37 - 1.42 g/cc	0.0495 - 0.0513 lb/in³	Molding; IS 867-1963
Apparent Bulk Density	0.640 - 0.700 g/cc	0.0231 - 0.0253 lb/in³	IS 867-1963
Water Absorption	0.20 - 0.60 %	0.20 - 0.60 %	IS 13411-1993
Linear Mold Shrinkage	0.0060 - 0.0077 cm/cm	0.0060 - 0.0077 in/in	IS 13411-1992

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	46.0 - 55.0 MPa	6670 - 7980 psi	5 mm/min.; IS 867-1963
Shear Strength	66.0 - 75.0 MPa	9570 - 10900 psi	2mm/min.; IS 867-1963
Izod Impact, Notched	0.220 - 0.300 J/cm	0.412 - 0.562 ft-lb/in	IS 13411-1992

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+11 - 3.16e+11 ohm-cm	1.00e+11 - 3.16e+11 ohm-cm	IS 3396-1979
Surface Resistance	1.00e+10 - 3.16e+10 ohm	1.00e+10 - 3.16e+10 ohm	IS 3396-1979
Dielectric Strength	4.00 - 5.00 kV/mm @Temperature 90.0 °C	102 - 127 kV/in @Temperature 194 °F	IS 2584-1963

Processing Properties	Metric	English	Comments
Mold Temperature	160 - 170 °C	320 - 338 °F
Injection Pressure	15.68 - 34.3 MPa	2274 - 4970 psi	Mold Pressure
Cure Time	0.333 - 0.500 min	0.00556 - 0.00833 hour	per mm
Shelf Life	1.50 Month	1.50 Month	27-30°C
	4.00 Month	4.00 Month	below 20°C