Albis Plastics Cellulose Acetate CA700 , Unreinforced, 31% Plasticizer (discontinued **)

Category	Polymer , Renewable/Recycled Polymer , Thermoplastic , Cellulosic , Cellulose Acetate, Molded
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Albis Plastics Cellulose Acetate CA700 , Unreinforced, 31% Plasticizer (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Amorphous Cellulose Acetate (CA)Characteristics: Chemical Resistance, Toughness, Strength, Hardness, Gloss, Clarity and "Feel"Applications: Tool Handles, Optical Products, Toys and Sheet ProductsProcessing: Injection Molding (Melt Temperature: 470°F, Mold Temperature: 160°F)Data supplied by ALBIS Plastics Corporation.

Physical Properties	Metric	English	Comments
Density	1.27 g/cc	0.0459 lb/in³	ASTM D792
Water Absorption	2.3 %	2.3 %	(24 hr); ASTM D570
Linear Mold Shrinkage	0.0020 - 0.0060 cm/cm	0.0020 - 0.0060 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	36.5 MPa	5290 psi	ASTM D638
Tensile Strength, Yield	31.0 MPa	4500 psi	ASTM D638
Flexural Yield Strength	42.1 MPa	6110 psi	ASTM D790
Flexural Modulus	1.38 GPa	200 ksi	ASTM D790
Izod Impact, Notched	1.87 J/cm	3.50 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	66.0 °C	151 °F	ASTM D648
Vicat Softening Point	108 °C	226 °F	ASTM D1525

Processing Properties	Metric	English	Comments
Melt Temperature	224 °C	435 °F	Injection Molding
Mold Temperature	54.0 °C	129 °F