Albis Plastics Cellulose Acetate Butyrate B9004 (Odor Mask Added), 5% Plasticizer  (discontinued **)

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Cellulosic , Cellulose Acetate Butyrate, Molded
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Albis Plastics Cellulose Acetate Butyrate B9004 (Odor Mask Added), 5% Plasticizer  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and ToysProcessing: Injection Molding (Melt Temperature: 470°F, Mold Temperature: 160°F)Data supplied by Albis Plastics Corporation.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ASTM D792
Water Absorption 1.6 %
1.6 %
(24 hr); ASTM D570
Linear Mold Shrinkage 0.0020 - 0.0060 cm/cm
0.0020 - 0.0060 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 44.1 MPa
6400 psi
ASTM D638
Tensile Strength, Yield 36.5 MPa
5290 psi
ASTM D638
Flexural Yield Strength 45.5 MPa
6600 psi
ASTM D790
Flexural Modulus 1.38 GPa
200 ksi
ASTM D790
Izod Impact, Notched 1.49 J/cm
2.79 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 83.0 °C
181 °F
ASTM D648
Vicat Softening Point 115 °C
239 °F
ASTM D1525
Flammability, UL94 HB
HB
0.125 in
Processing Properties Metric English Comments
Melt Temperature 243 °C
469 °F
Injection
Mold Temperature 71.0 °C
160 °F