Akro-Plastic Akromid® B3 GF 10 (2829) PA 6 Conditioned, 10% Glass Filled

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled
Manufacturer Akro-Plastic
Trade Name Akromid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Akro-Plastic Akromid® B3 GF 10 (2829) PA 6 Conditioned, 10% Glass Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AKROMID® B (Polyamide 6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperatures as well as easy processing. AKROMID® B is an engineering plastic compound that allows a broad range of possible applications. On the basis of these standard types, we are able to develop individual compounds for special application needs.Information from Akro-Plastic
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Filler Content 10 %
10 %
ISO 1172
Water Absorption 2.6 - 3.4 %

@Temperature 70.0 °C
2.6 - 3.4 %

@Temperature 158 °F
62% r.h., Humidity; ISO 62
Water Absorption at Saturation 8.5 - 9.0 %

@Time 82800 sec
8.5 - 9.0 %

@Time 23.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa
7980 psi
5 [mm/min]; ISO 527-1/2
27.5 MPa

@Temperature 160 - 175 °C,
Time 1.80e+7 sec
3990 psi

@Temperature 320 - 347 °F,
Time 5000 hour
5 [mm/min], 50% Loss of Tensile Strength; ICE 216
27.5 MPa

@Temperature 130 - 150 °C,
Time 7.20e+7 sec
3990 psi

@Temperature 266 - 302 °F,
Time 20000 hour
5 [mm/min], 50% Loss of Tensile Strength; ICE 216
Elongation at Break 17 %
17 %
5 [mm/min]; ISO 527-1/2
Tensile Modulus 2.70 GPa
392 ksi
1[mm/min]; ISO 527-1/2
Charpy Impact Unnotched 11.5 J/cm²

@Temperature 23.0 °C
54.7 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.800 J/cm²

@Temperature 23.0 °C
3.81 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
ISO 11357-1/3
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+10 ohm-cm
1.00e+10 ohm-cm
IEC 60093
Surface Resistance 1.00e+10 ohm
1.00e+10 ohm
IEC 60093