Adell AR-13 Nylon 66, 15% Glass Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | Adell Plastics, Inc. |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Adell AR-13 Nylon 66, 15% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Adell Plastics, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| Water Absorption | 1.0 % | 1.0 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0055 cm/cm | 0.0055 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 95 | 95 | ASTM D785 |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Ultimate | 107 MPa | 15500 psi | ASTM D638 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM D638 |
| Flexural Strength | 172 MPa | 24900 psi | ASTM D790 |
| Flexural Modulus | 4.80 GPa | 696 ksi | ASTM D790 |
| Compressive Yield Strength | 179 MPa | 26000 psi | ASTM D695 |
| Izod Impact, Notched | 0.500 J/cm | 0.937 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263 °C | 505 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 238 °C | 460 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 441 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
Users viewing this material also viewed the following:
- MV Labs RH480 [RhCl(C6H5)3P)3] Chlorotris(triphenylphosphine)rhodium(I)
- Gromax BTG30-FN03N1 Nylon 6 30% Glass Filled (Conditioned)
- Lucas-Milhaupt Silvabrite® Lead-Free Solder
- Mitsui ADMER® NF498A PE Type Polyolefin
- Lanxess Durethan® BM 240 H2.0 901510 Nylon 6, 40% Mineral
- SABIC Innovative Plastics LNP THERMOCOMP ZX08309 PPE+HIPS (Asia Pacific)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 6.0 PHR DBPH-50
- A. Schulman POLYBATCH™ Blue LL40348/4 Concentrate Based In LLDPE
- ExxonMobil LLDPE LL 8555.24 Linear Low Density Polyethylene Resin
- Arlon 41600R025 0.025" Uncured, Unsupported Silicone Rubber on Release Carrier
Copyright © lookpolymers.com All Rights Reserved