Adamas Rixon 130 PEEK, 30% Carbon Filled
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled |
| Manufacturer | Adamas |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Adamas Rixon 130 PEEK, 30% Carbon Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Adamas, HPM
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 - 1.44 g/cc | 1.41 - 1.44 g/cc | ASTM D792 |
| Water Absorption | 0.15 - 0.18 % | 0.15 - 0.18 % | Immersion 24 hrs; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 93 - 95 | 93 - 95 | ASTM D785 |
| Hardness, Shore D | 85 - 90 | 85 - 90 | ASTM D2240 |
| Ball Indentation Hardness | 330 - 350 MPa | 47900 - 50800 psi | ISO 2032-N961 |
| Tensile Strength at Break | 110 - 140 MPa | 16000 - 20300 psi | ASTM D638 |
| Elongation at Break | 2.0 - 4.0 % | 2.0 - 4.0 % | ASTM D638 |
| Tensile Modulus | 1.00 - 1.10 GPa | 145 - 160 ksi | ASTM D638 |
| Flexural Strength | 200 - 220 MPa | 29000 - 31900 psi | 3.5% flexural stress; ASTM D4894 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 343 °C | 649 °F | DSC |
| Maximum Service Temperature, Air | 250 °C | 482 °F | DSC |
| Minimum Service Temperature, Air | -80.0 °C | -112 °F | DSC |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+6 ohm-cm | 1.00e+6 ohm-cm | ASTM D257 |
| Surface Resistance | 1e+05 | 1e+05 | ASTM D257 |
Users viewing this material also viewed the following:
- Nye Lubricants 368AS (RL) Synthetic Oil
- Polymax® Maxelast® P3936C TPE, PP Overmold or Standalone use
- Premix Thermoplastics PREBLACK CP 731-40 Black Universal Masterbatch, 40% Carbon Black
- Formosa Plastics Formolene® HL5505 Blow Molding HDPE (discontinued **)
- Karina E CAK 85-48/1-F Black PVC Compound
- LyondellBasell Petrothene® LM600700 High Density Polyethylene (Blow Molding Grade)
- Styron CALIBREâ„¢ 2061-15 Polycarbonate
- Dow AMPLIFY™ VA 400 Ethylene vinyl acetate (EVA)
- 3M 7743FL Polyester Overlaminating Film
Copyright © lookpolymers.com All Rights Reserved