- Adamas Adalon® 413 PTFE, 20% PPS
Adamas Adalon® 413 PTFE, 20% PPS
| Category | Polymer , Thermoplastic , Fluoropolymer , PTFE |
| Manufacturer | Adamas |
| Trade Name | Adalon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Adamas Adalon® 413 PTFE, 20% PPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Adamas, HPM
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 2.11 - 2.12 g/cc | 2.11 - 2.12 g/cc | ASTM D792 |
| Deformation | 8.5 - 11 % | 8.5 - 11 % | ASTM D621 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 56 - 59 | 56 - 59 | ASTM D2240 |
| Ball Indentation Hardness | 47.0 - 50.0 MPa | 6820 - 7250 psi | ISO 2032-N132 |
| Tensile Strength at Break | >= 25.0 MPa | >= 3630 psi | ASTM D4745-97 |
| Elongation at Break | >= 170 % | >= 170 % | ASTM D4745-97 |
| Tensile Modulus | >= 0.0300 GPa | >= 4.35 ksi | ASTM D4745-97 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.380 W/m-K | 2.64 BTU-in/hr-ft²-°F | ASTM C 177 |
| Melting Point | 327 °C | 621 °F | DSC |
| Maximum Service Temperature, Air | 220 °C | 428 °F | DSC |
| Minimum Service Temperature, Air | -50.0 °C | -58.0 °F | DSC |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | ASTM D257 |
| Dielectric Constant | 1.5 @Frequency 60.0 - 2.00e+6 Hz |
1.5 @Frequency 60.0 - 2.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 25.0 - 30.0 kV/mm | 635 - 762 kV/in | ASTM D149 |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 9007 BLK
- Arlon Thermabond® R37340X008 Primerless Electronic Adhesive (discontinued **)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 120 PHR Mistron Vapor Filler
- Hogen Duralloy H5TC 50 Tungsten Carbide/50 Copper PM Metal Composite
- M Chemical GUARD DOGâ„¢ UVP Benzotriazole UV Absorber
- H.C. Starck Glass Melting Electrodes made from Electron Beam Melted Molybdenum
- UBE 7034T Nylon 6/12 Monofilament (Drawing Ratio=5.5, Diameter 0.4 mm)
- Bulk Molding Compounds BMC 620X Mineral Filled, Glass Fiber Reinforced Polyester Compound
- Asahi Kasei ASACLEAN UP Sun Plastech Purging Compound
Copyright © lookpolymers.com All Rights Reserved