- Adamas Adalon® 125 PTFE, 35% Carbon Filled
Adamas Adalon® 125 PTFE, 35% Carbon Filled
| Category | Polymer , Thermoplastic , Fluoropolymer , PTFE , Polytetrafluoroethylene (PTFE), Carbon Fiber Filled |
| Manufacturer | Adamas |
| Trade Name | Adalon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Adamas Adalon® 125 PTFE, 35% Carbon Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Adamas, HPM
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 2.03 - 2.05 g/cc | 2.03 - 2.05 g/cc | ASTM D792 |
| Deformation | 2.0 - 3.1 % | 2.0 - 3.1 % | Permanent deformation after 24 hrs @ 23°C; ASTM D621 |
| 4.4 - 5.5 % | 4.4 - 5.5 % | ASTM D621 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 58 - 62 | 58 - 62 | ASTM D2240 |
| Tensile Strength at Break | >= 15.0 MPa | >= 2180 psi | ASTM D4894 |
| Elongation at Break | >= 40 % | >= 40 % | ASTM D4894 |
| Coefficient of Friction, Dynamic | 0.13 - 0.15 | 0.13 - 0.15 | ASTM D1894 |
| Coefficient of Friction, Static | 0.14 - 0.16 | 0.14 - 0.16 | ASTM D1894 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.270 W/m-K | 1.87 BTU-in/hr-ft²-°F | ASTM C 177 |
| Melting Point | 327 °C | 621 °F | DSC |
| Maximum Service Temperature, Air | 260 °C | 500 °F | DSC |
| Minimum Service Temperature, Air | -80.0 °C | -112 °F | DSC |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10000 ohm-cm | 10000 ohm-cm | ASTM D257 |
| Surface Resistance | 1000 ohm | 1000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Network Polymers NPP 11-0535
- Pyrotek PROSILY G-10R Graphite Lubricant/Coating
- Indorama AlphaPet Preformance® 1708CC(A) PET Resin
- Haynes 556® alloy, bar, after 4000 hours at 760°C (1400°F)
- SABIC Innovative Plastics NORYL GTX RNX130 PPE+PS+PA
- A. Schulman POLYBATCH™ Navajo 10294U/4 Concentrate Based In LLDPE
- Elektro-Isola Etronax MFP G Phenolic, Cotton Fabric Reinforcement, Black, Tubes
- Axiall 19740 Wire & Cable Flexible PVC
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 20 PHR N550 (FEF) Filler
Copyright © lookpolymers.com All Rights Reserved