Aclo Accutech Polypropylene Homopolymer HP0334G20M10CL Glass/Mineral Reinforced Coupled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Glass/Mineral Reinforced |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0334G20M10CL Glass/Mineral Reinforced Coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | MD; ASTM D955 |
| Melt Flow | 1.5 g/10 min | 1.5 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 90 | 90 | ASTM D785 |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ASTM D638 |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 3.499 GPa | 507.5 ksi | ASTM D638 |
| Flexural Strength | 77.98 MPa | 11310 psi | ASTM D790 |
| Flexural Modulus | 4.200 GPa | 609.1 ksi | ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm | 1.10 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F |
Users viewing this material also viewed the following:
- Taiwan Sheen Soon Sheenthane® A9513H TPU for Ink
- Teknor Apex Monprene® MP-1881E Thermoplastic Elastomer
- Tipco Tipcolene® FPT 30 PPC - 30% Talc Reinforced Polypropylene Copolymer Compound
- A. Schulman POLYBATCH™ Dark Grey LL80362/4 Concentrate Based In LLDPE
- Crucible Steel HALCOMB® 218 Tool Steel, AISI H11
- ExxonMobil HDPE HD 7800P High Density Polyethylene Copolymer Resin
- DuPont Teijin Films Melinex® 377 Polyester Film, 200 Gauge
- ACC EP RAP-1567 HX EPI Engineered Polymers Aliphatic Polyurea
- Poco Graphite TM Industrial Grade Graphite
- Plaslok 308 Black (INJ) Mineral/Flock Filled Phenolic Molding Compound (discontinued **)
Copyright © lookpolymers.com All Rights Reserved