- Aclo Accutech Polypropylene Homopolymer HP0334G20CL Glass Reinforced Coupled
Aclo Accutech Polypropylene Homopolymer HP0334G20CL Glass Reinforced Coupled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Glass Fiber Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0334G20CL Glass Reinforced Coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | MD; ASTM D955 |
| Melt Flow | 5.0 g/10 min | 5.0 g/10 min | ASTM D1238 |
| Ash | 20 % | 20 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 96 | 96 | ASTM D785 |
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ASTM D638 |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 2.899 GPa | 420.5 ksi | ASTM D638 |
| Flexural Strength | 71.98 MPa | 10440 psi | ASTM D790 |
| Flexural Modulus | 3.699 GPa | 536.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.438 J/cm | 0.820 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C | 270 °F |
Users viewing this material also viewed the following:
- Taiwan PU Corporation TPUI-T85 Transparent Grade, Injection Molding Polyester Base TPU
- Shandong Dongyue Shenzhou New Material Co CHF105 Perfluorosulfonic Acid Ion-Exchange Resin (PFSA)
- UBE Tyranno Grade S Ceramic High Temperature Fiber
- DuPont Elvax® 350 Ethylene Vinyl Acetate
- Total HDPE 5802 High Density Polyethylene - Blow Molding
- Total PPC 4820WZ Polypropylene, Impact Copolymer
- Loctite® Varidot™ 3617 Stencil Print
- Entec Hypro™ PPC-GF10 Natural Impact Polypropylene, 10% Glass Reinforced
- Arlon 25662T010 0.010" (0.254 mm) Cured Silicone Rubber with Laminated ETFE Film Substrate
- Ascend Performance Materials Vydyne® R543H Natural Nylon 66, 43% Glass Reinforced, DAM
Copyright © lookpolymers.com All Rights Reserved