Aclo Accutech Polypropylene Copolymer CP0437W10L1 Wollastonite Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Copolymer CP0437W10L1 Wollastonite Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | MD; ASTM D955 |
| Melt Flow | 18 g/10 min | 18 g/10 min | ASTM D1238 |
| Ash | 10 % | 10 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 57 | 57 | ASTM D785 |
| Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM D638 |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 1.100 GPa | 159.5 ksi | ASTM D638 |
| Flexural Strength | 20.0 MPa | 2900 psi | ASTM D790 |
| Flexural Modulus | 0.8998 GPa | 130.5 ksi | ASTM D790 |
| Izod Impact, Notched | 2.99 J/cm | 5.60 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 51.1 °C | 124 °F |
Users viewing this material also viewed the following:
- Murlin BCP 600 Aluminum Grade Bone Ash Mold Release
- RedEye On Demand Polyphenylsulfone (PPSF), Rapid Prototyping Material
- Honeywell Capran® 996 Heat Stabilized Nylon Film (discontinued **)
- Saint-Gobain CHR® A603 Aluminum Foil Backing Acrylic Adhesive Pressure Sensitive Tape
- Cossa Polimeri ESTABLEND 8500 Polycarbonate ABS Blend
- CIMBAR MV 607 Talc
- Arlon 0.008" (0.2032 mm) Primerless Thermabond® Uncured Silicone (99990A008)
- Arlon 18986XA023 0.023" Uncured/Cured Silicone Rubber with Fiberglass Substrate
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR N330 Filler
Copyright © lookpolymers.com All Rights Reserved