- Aclo Accutech Polypropylene Copolymer CP0437G10M20CL Glass/Mineral Reinforced Coupled
Aclo Accutech Polypropylene Copolymer CP0437G10M20CL Glass/Mineral Reinforced Coupled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Glass/Mineral Reinforced |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Copolymer CP0437G10M20CL Glass/Mineral Reinforced Coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | MD; ASTM D955 |
| Melt Flow | 9.0 g/10 min | 9.0 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 60 | 60 | ASTM D785 |
| Tensile Strength at Break | 26.0 MPa | 3770 psi | ASTM D638 |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 2.699 GPa | 391.5 ksi | ASTM D638 |
| Flexural Strength | 40.0 MPa | 5800 psi | ASTM D790 |
| Flexural Modulus | 2.899 GPa | 420.5 ksi | ASTM D790 |
| Izod Impact, Notched | 1.23 J/cm | 2.30 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F |
Users viewing this material also viewed the following:
- Nylene® PA6/6 Glass Filled 5143 HS Nylon 6/6
- H.C. Starck MoMP 3.5 - 4.5 micron Molybdenum Metal Powder, Mo (99.95%)
- Styron EMERGEâ„¢ 4530-10 Polycarbonate
- Chase Plastics CP Pryme® N320L (Dry) Nylon 6, 20% Glass Fiber Reinforced, Lubricated, Recycled Content
- 3M 3028EK Double Coated Tapes with Adhesive 350
- BASF Ultradur B 4040 G10 High Speed BK15029 50% Glass Filled PBT/PET
- Ashley Polymers Ashlene® ABS Resin F-217
- ConocoPhillips Hydroclear® 10 Ultra-Clean Spindle Oil
- Kuraray Genestar™ GN2450 Nylon, 45% Glass Filled
Copyright © lookpolymers.com All Rights Reserved