Aclo Accutech Polypropylene Copolymer CP0437C40L1 Calcium Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Calcium Carbonate (CaCO3) Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Copolymer CP0437C40L1 Calcium Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.196 g/cc | 0.04321 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | MD; ASTM D955 |
| Melt Flow | 20 g/10 min | 20 g/10 min | ASTM D1238 |
| Ash | 40 % | 40 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 45 | 45 | ASTM D785 |
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 |
| Tensile Strength, Yield | 13.0 MPa | 1890 psi | ASTM D638 |
| Elongation at Break | 20 % | 20 % | ASTM D638 |
| Elongation at Yield | 2.0 % | 2.0 % | ASTM D638 |
| Tensile Modulus | 1.500 GPa | 217.5 ksi | ASTM D638 |
| Flexural Strength | 17.0 MPa | 2470 psi | ASTM D790 |
| Flexural Modulus | 1.40 GPa | 203 ksi | ASTM D790 |
| Izod Impact, Notched | 4.00 J/cm | 7.50 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 77.8 °C | 172 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 51.1 °C | 124 °F |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable W1213 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Mytex Polymers AS33L(W)-06 Polypropylene, Rubber modified, Talc filled, Compounded
- Ipiranga Petrochem HC 7260 HDPE
- H.C. Starck Amperit® 827.054 Zirconium Oxide-Yttrium Oxide 93-7 (ZrO2-Y2O3)
- Supreme Petrochem SC 201LV General Purpose Polystyrene
- Teknor Apex Tekbond® TB 1139A Thermoplastic Elastomer
- Asahi Kasei Thermofil N7-9900-1600 Unreinforced, High Impact, Heat Stabilized
- ACC QLE 1035 QSI Quantum Silicones 38 Durometer Addition Cure Elastomer for Coating
- BASF Ultramid® A3EG7 35% Glass Filled PA66 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved