- Aclo Accutech Polyethylene HD0234G10UVL High Density Glass Reinforced UV Stabilized
Aclo Accutech Polyethylene HD0234G10UVL High Density Glass Reinforced UV Stabilized
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Glass fiber Filled |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polyethylene HD0234G10UVL High Density Glass Reinforced UV Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.00 g/cc | 0.0361 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | MD; ASTM D955 |
| Melt Flow | 5.0 g/10 min | 5.0 g/10 min | ASTM D1238 |
| Ash | 10 % | 10 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 50 | 50 | ASTM D785 |
| Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM D638 |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | ASTM D638 |
| Elongation at Break | 165 % | 165 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 2.050 GPa | 297.3 ksi | ASTM D638 |
| Flexural Strength | 29.0 MPa | 4210 psi | ASTM D790 |
| Flexural Modulus | 1.700 GPa | 246.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 119 °C | 246 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS (Asia Pacific)
- Michelman® Michem® Lube 182 Anionic carnauba/paraffin wax emulsion
- Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick
- Teknor Apex Sinvicomp SIM 5000 Polyvinyl Chloride, Flexible
- A. Schulman POLYBATCH™ Yellow 2600V Concentrate Based In Polyethylene
- BASF Neopor® 2300 Expandable Polystyrene
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 60 PHR Non-Black, Aerosil 200
Copyright © lookpolymers.com All Rights Reserved