- Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled
- Aclo Accutech ABS ABS831G30L Glass Reinforced
Aclo Accutech ABS ABS831G30L Glass Reinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech ABS ABS831G30L Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | MD; ASTM D955 |
| Melt Flow | 0.70 g/10 min | 0.70 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength at Break | 75.98 MPa | 11020 psi | ASTM D638 |
| Tensile Strength, Yield | 75.98 MPa | 11020 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 4.899 GPa | 710.6 ksi | ASTM D638 |
| Flexural Strength | 100 MPa | 14500 psi | ASTM D790 |
| Flexural Modulus | 7.9986 GPa | 1160.1 ksi | ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm | 1.30 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 98.9 °C | 210 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 91.1 °C | 196 °F |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible XV3782 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Solvay Engineered Polymers SEQUEL® 1514 Engineered Polyolefin (discontinued **)
- Termopol Termoton® K4GA4070A TPE Compound, based on SEBS and Polyolefins
- Arlon 18146R026 0.026" (0.66 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Adell BT-37 Nylon 6, 35% Glass Reinforced; Impact Modified
- Alliance A-3 Alnico Magnetic Material
- A. Schulman ComAlloy Hiloy® 513 Polycarbonate, Glass Reinforced, UL
Copyright © lookpolymers.com All Rights Reserved